Specific Process Knowledge/Thermal Process/A3 Phosphor Drive-in furnace

From LabAdviser

Feedback to this page: click here


Phosphorus Drive-in furnace (A3)

Phosphorus Drive-in furnace (A3). Positioned in cleanroom B-1

The Phosphorus Drive-in furnace (A3) is a Tempress horizontal furnace for thermal oxidation of silicon wafers. Furthermore, the furnace is used for phosphorus drive-in afte pre-deposition/doping or after boron ion implantation.

The furnace is mostly used for wet and dry thermal oxidation of silicon wafers. The oxidation recipes are named e.g. "WET1000" and "DRY1000", where "WET" or "DRY" indicates whether it is a wet or dry oxidation process, and the number indicates the oxidation temperature.

The purpose of phosphorus doping is to make conductive structures, etch stop layers etc. After a phosphorus pre-deposition/doping or ion implantation process, a drive-in process with or without an oxide growth is done in the furnace. The phosphorus pre-deposition is normally done in the Phosphorus Pre-dep (A4) furnace, and ion implantation have to be done elsewhere.

The Phosphorus Drive-in furnace is the third furnace tube in the A-stack positioned in cleanroom B-1. The furnaces in the A-stack are the cleanest of all furnaces in the cleanroom. Please be aware of that all wafers have to be RCA cleaned before they enter the furnace (except wafers coming form the Phosphorus Pre-dep furnace that have been BHF etched in the dedicated bath in the RCA bench), and please check the cross contamination information in LabManager, before you use the furnace.


The user manual, quality control instruction and results, technical information and contact information can be found in LabManager:

Phosphorus Drive-in furnace (A3)

Process knowledge

Quality Control - Recipe Parameters and Limits

Quality Control (QC) for the processes "Wet1050" and "Dry1050"
QC Recipe: Wet1050 Dry1050
H2 flow 3 slm 0 slm
O2 flow 2 slm 5 slm
Temperature 1050 C 1050 C
Oxidation time 30 min 100 min
QC limits Thickness Non-uniformity (both over a single wafer

and over the boat)

Dry1050 110-116 nm 3 %
Wet1050 305-321 nm 5 %


Overview of the performance of the phosphorus drive-in furnace and some process related parameters

Purpose
  • Drive-in of phosphorous
  • Oxidation of silicon
  • Oxidation of phosphorous phase layers
 Oxidation:
  • Dry
  • Wet: with torch (H2+O2)
Performance Film thickness
  • Dry SiO2: 50 Å to ~2000 Å (it takes too long to grow a thicker oxide layer)
  • Wet SiO2: 50 Å to ~3 µm (it takes too long to grow a thicker oxide layer)
Process parameter range Process Temperature
  • 800-1150 oC
Process pressure
  • 1 atm
Gasses on the system
  • O2, N2 and H2
Substrates Batch size
  • 1-30 100 mm wafers (or 50 mm wafers) per run
Substrate materials allowed
  • Silicon wafers (RCA cleaned)
  • Wafers from the the Phosphorus Pre-dep furnace can go directly into the furnace
Retrieved from "https://labadviser.nanolab.dtu.dk//index.php?title=Specific_Process_Knowledge/Thermal_Process/A3_Phosphor_Drive-in_furnace&oldid=34136"