Specific Process Knowledge/Lithography/UVLithography: Difference between revisions
| Line 117: | Line 117: | ||
|[[Specific_Process_Knowledge/Lithography/Coaters#KS Spinner|KS Spinner]] | |[[Specific_Process_Knowledge/Lithography/Coaters#KS Spinner|KS Spinner]] | ||
|Thickness and process dependent. | |Thickness and process dependent. | ||
Refer to process datasheet and literature. | |||
|mr-Dev 600 developer (PGMEA) | |mr-Dev 600 developer (PGMEA) | ||
|IPA | |IPA | ||
Revision as of 12:35, 28 March 2014
Feedback to this page: click here
UV Lithography uses ultraviolet light to transfer a pattern from a mask to a wafer coated with photoresist. The photoresist film is spin coated on the wafers and the pattern is transferred to the wafer by using a mask aligner. DTU Danchip houses a number of automatic or semi-automatic coaters and mask aligners.
Resist Overview
| Resist | Polarity | Manufacturer | Comments | Technical reports | Spin Coating | Exposure dose | Developer | Rinse | Remover | Process flows (in docx-format) |
| AZ 5214E | Positive but can be reversed | AZ Electronic Materials | Can be used for both positive and reverse processes with resist thickness between 1 to 4um. | AZ5214E.pdf | SSE, KS Spinner, III-V Spinner | Positive process:
23-33 mJ/cm2 per µm resist for i-line. ½ dose for broadband exposure. Reverse process: 10.5 mJ/cm2 per µm resist for i-line, followed by 210 mJ/cm2 flood exposure after reversal bake. ½ dose for broadband exposure. |
AZ 351B developer | DI water | Acetone | |
| AZ 4562 | Positive | AZ Electronic Materials | For process with resist thickness between 6 and 25um. | AZ4500.pdf | SSE, KS Spinner | 28 mJ/cm2 per µm resist for i-line, probably increasing with increasing thickness.
Multiple exposure recommended. ½ dose for broadband exposure. |
AZ 351B developer | DI water | Acetone | Process_Flow_thick_AZ4562.docx |
| AZ MiR 701 | Positive | AZ Electronic Materials | High selectivity for dry etch. | AZ_MiR_701.pdf | Spin Track 1 + 2 | Preliminary results:
105 mJ/cm2 per µm resist for i-line. 1/5 dose for broadband exposure. |
AZ 726 MIF developer | DI water | Remover 1165 | Process_Flow_AZ_MiR701.docx |
| AZ nLOF 2020 | Negative | AZ Electronic Materials | AZ_nLOF_2020.pdf | Spin Track 1 + 2 | <30 mJ/cm2 per µm resist for i-line, decreasing with increasing thickness.
Same dose for broadband exposure. |
AZ 726 MIF developer | DI water | Remover 1165 | Process_Flow_AZ_nLOF_2020.docx | |
| SU-8 | Negative | Microchem | SU-8_DataSheet_2005.pdf, SU-8_DataSheet_2075.pdf | KS Spinner | Thickness and process dependent.
Refer to process datasheet and literature. |
mr-Dev 600 developer (PGMEA) | IPA | Plasma ashing can remove crosslinked SU8. | Process_Flow_SU8_70um.docx |