Specific Process Knowledge/Thermal Process/Resist Pyrolysis furnace

From February 2024: RESIST PYROLYSIS FURNACE

Feedback to this page: click here

This page is written by DTU Nanolab internal

The Resist Pyrolysis furnace

From February 2024: The name of the furnace has changed from Multipurpose Anneal Furnace to Resist Pyrolysis Furnace. At the same time, the furnace has become a research tool. This means, that the furnace is mainly available for users working on certain research projects at DTU Nanolab, and it should mainly be used for resist pyrolysis

The Resist Pyrolysis furnace it made by ATV Technologie, and it was installed in the cleanroom in 2015.

The furnace is mainly being used for resist pyrolysis (see the next section). It can also be used for annealing in nitrogen (N2) and oxidation with oxygen (O2), but O2 is mostly used for cleaning of the furnace after resist pyrolysis.

Process steps can run either in vacuum or at atmospheric pressure. A small N2 or O2 flow (up to 2 slm) can be applied in vacuum steps.

The quartz parts in the furnace can be changed, depending on what processes and samples the furnace is used for, but it been decided that a quartz set for resist resist pyrolysis will be mounted in the furnace all the time. This limits the number of materials that are allowed in the furnace (see section 7.2).

All process gasses (except purge nitrogen) are heated, before they are introduced into the furnace at the door side.

The furnace tube is heated by use of 12 long heaters situated along the furnace tube and combined in three groups (top, bottom left and bottom right) and two flat heaters situated in the ends of the furnace tube. The this way the temperature will be very uniform everywhere in the furnace tube. The heating can be done very fast, up to 30 ^oC/min. For atmospheric pressure processes the maximum temperature is 1100 ^oC, and for vacuum processes the maximum temperature is 1050 ^oC.

The furnace body surrounding the furnace tube consists of a top and bottom half-shell. To cool down the furnace (when the temperature is below 800 ^oC), the top half shelf can be lifted up, and cooling fans will then flow air from the surroundings around the furnace tube to cool it down. However, for safety reasons, the cooling fans will not the activated when there is hydrogen in the furnace, and cooling will then be very slow.

It is not possible to open the furnace when the temperature is above 300 ^oC.

For resist pyrolysis, samples with different resist layers are heated up to maximum 1100 ^oC in a nitrogen atmosphere. At high temperatures carbon is formed by pyrolysis of the resist. In this way conductive structures can be made from a resist patterned sample. If oxygen from the air or from outgassing of the resist is present in the furnace, the resist layer will be removed, thus it is important to evacuate the furnace and flush it with nitrogen, before a high temperature for resist pyrolysis is obtained. Pyrolysis of a large amount of resist may also be a problem due to resist outgassing.

The user manual, technical information and contact information can be found in LabManager:

Furnace: Multipurpose annealing

Process information

Oxidation: look at the Oxidation page
Annealing: look at the Annealing page
Results from the Multipurpose Anneal Furnace acceptance test
Pyrolysis

Overview of the performance of the ATV furnace and process related parameters

Purpose		Dry oxidation of silicon Annealing in N₂, H₂ or a mixture of the two gasses Pyrolysis of different resists
Performance	Film thickness	Dry oxidation: 50 Å to ~200 nm SiO₂ (it takes too long to grow a thicker oxide layer)
Process parameter range	Process Temperature	No vacuum: 25 ^oC - 1100 ^oC Vacuum: 25 ^oC - 1050 ^oC
	Process pressure	1 atm Vacuum down to ~0.1 mbar (depends on gas flow)
	Gasses on the system	N₂: 20 slm O₂: 10 slm H₂: 5 slm (max 2 slm for vacuum processes) N₂ mix : 10 slm (for H₂-N₂ gas mixture)
Substrates	Batch size	1-30 50 mm, 100 mm or 150 mm wafers per run 1-50 200 mm wafers per run (not possible with all quartz sets) Smaller samples (placed on Si carrier wafers)
Substrates	Substrate materials allowed	Depends on the quartz set