Specific Process Knowledge/Thin film deposition/Deposition of Chromium

From LabAdviser

Feedback to this page: click here

Unless otherwise stated, this page is written by DTU Nanolab internal

Studies of Cr deposition processes

Uniformity of Cr layers - Uniformity of Cr layers deposited with different methods and settings

Sputtering of Cr in Wordentec - Settings and deposition rates

Sputtering of Cr in Sputter system (Lesker) - Settings and deposition rates

Sputtering of Cr in Sputter-system Metal-Oxide (PC1) - Settings and deposition rates

Sputtering of Cr in Sputter-system Metal-Nitride (PC3) - Settings and deposition rates

Thermal evaporation of Cr in Thermal evaporator - Settings and deposition results

Stress in sputtered Cr films - Extremely high tensile stress in Cr films deposited at high temperature


Chromium deposition

Chromium can be deposited by e-beam evaporation, thermal evaporation, and sputter deposition. It should be noted that in e-beam evaporation, chromium does not melt but evaporates directly from the solid phase. In the chart below you can compare the different deposition equipment. Further down you will find the results of some studies on chromium deposition.

E-beam evaporation E-beam evaporation (E-beam evaporator (Temescal) and E-beam evaporator (10-pockets)) E-beam evaporation and sputter deposition (Wordentec) Thermal evaporation (Thermal evaporator) Sputter deposition (Lesker sputterer) Sputter deposition ((Sputter-system Metal-Oxide (PC1) and Sputter-system Metal-Nitride (PC3)) )
General description E-beam deposition of Chromium E-beam and sputter deposition of Chromium Thermal deposition of Chromium Sputter deposition of Chromium Sputter deposition of Chromium
Pre-clean Ar ion gun (only in E-beam evaporator Temescal) RF Ar clean RF Ar clean RF Ar clean
Layer thickness 10Å to 1µm* 10Å to 1µm* 80 nm at least up to 200 nm at least up to 200 nm
Deposition rate 1 Å/s to 10 Å/s 1 Å/s to 10 Å/s (e-beam)

Sputtering: Depends on process parameters. See here and process log.

1 Å/s Depends on process parameters. At least up to 1.48 Å/s. See process log. Depends on process parameters.
Batch size
  • 4x6" wafers or
  • 3x8" wafers (ask for holder)
  • Many smaller pieces
  • 24x2" wafers or
  • 6x4" wafers or
  • 6x6" wafers
  • 4x 2" wafer or
  • 1x 4" wafers or
  • 1x6" wafer or
  • Several smaller pieces
  • In theory up to 8" wafer (or 2x4" wafer) but uniformity will be bad
  • 1x6" wafers
  • Smaller pieces/wafers
  • up to 10x4" wafers or
  • up to 10x6" wafers or
  • many smaller samples
Allowed materials

Almost any that does not degas. See the cross-contamination sheet.

Almost any that does not degas. See the cross-contamination sheet.

Almost any that does not degas. See the cross-contamination sheet.

  • Silicon wafers
  • and almost any
  • Almost that does not degas - see cross contamination sheets for PC1 and PC3
  • Special carrier for III-V materials.
Comment Takes approx. 20 min to pump down Takes approx. 1 hour to pump down Takes approx. 20 min to pump down Takes approx. 5 min to pump down load lock and 6 min for transfer to processing chamber

* For thicknesses above 300 nm, please request permission from metal@nanolab.dtu.dk to ensure there is enough material.