Specific Process Knowledge/Lithography/LiftOff

Feedback to this page: click here

Lift-off Comparison Table

Equipment		Lift-off	Fume hood 03: Solvents
Purpose		Lift-off of e.g. metal using UV resists e-beam resists	General solvent work, including lift-off. DO NOT use other fume hoods for lift-off! Fume hood 04: Solvents Fume hood 08: III-V solvents Fume hood 09: UV development Fume hood 10: e-beam development
Bath chemical		NMP (Remover 1165) / Rinse in IPA	User defined
Process parameters	Process temperature	Heating of the bath is possible. The heating has been limited to 60°C	Heating is possible using portable hotplate or portable ultrasonic bath
	Ultrasonic agitation	Continuous or pulsed The power may be varied	Ultrasonic agitation is possible using portable ultrasonic bath
Substrates	Substrate size	100 mm wafers 150 mm wafers	In principle any, typically chips
	Allowed materials	Silicon or glass wafers Film or patterning of all but Type IV (Pb, Te)	Any cleanroom material
	Batch	1 - 25	1

Lift-off process

Schematic of the lift-off process.

The lift-off process is used to pattern a material that can be deposited as a film on a substrate. The material is patterned by depositing the film on top of a patterned masking material, which is then dissolved, thus leaving only parts of the substrate covered in the material. Although this may in theory be done using any combination of mask and material, the most common is using photoresist as a lift-off mask for metal.

The image to the left shows a schematic of the lift off process.

• 1. The substrate is coated with the masking material.
• 2. The masking material is patterned. The mask must be a negative image of the desired material pattern.
• 3. The material is deposited on top of both mask and substrate. The mask sidewall slope should be negative in order to prevent the material covering the sidewalls during deposition.
• 4. The masking material is dissolved, thus lifting part of the deposited material.
• 5. The remaining material forms the desired pattern on the substrate.

A successful lift-off process is dependent on many factors, including:

• Resist sidewall angle
• Resist thickness relative to the deposited material
• Layout of the design, especially the regions surrounding the device(s)

If the resist sidewall angle is positive, the deposited material will coat the sidewall, thus preventing the solvent from reaching and dissolving the resist. Ultrasonic agitation may be able to pierce the material deposited on top of resist, allowing lift-off. A a positive sidewall angle will typically result in a very slow lift-off process, as well as line edge roughness of the deposited material. A negative, or at least vertical, resist sidewall is usually needed for a successful lift-off process.

If the resist layer used for lift-off is too thin compared to the deposited layer, solvent access to the resist may be limited, due to partial or full coverage of the sidewalls. This would result in a slow lift-off, possibly with line edge roughness of the deposited material. As a rule of thumb, the resist should be 5-10 times thicker than the deposited material.

Small, tightly packed structures result in a very fast lift-off process. It is usually the big, uncovered areas between or around the device(s) that limit the lift-off speed. The less of the deposited material is to remain on the substrate after lift-off, the longer the sample has to spend in the lift-off solvent while resist under the deposited material is being dissolved and transported out. During the design of the pattern used for lift-off, it should be considered to fill any voids between devices with lift-off assisting dummy structures (e.g. hatching or squares/circles), in order to punctuate the open spaces, and allow for multiple, parallel starting points. Consider also if the edge of the substrate (exclusion zone) could be left covered with the deposited material.

Please note: At the DTU Nanolab cleanroom facility, it is only allowed to do lift-off in

• Lift-off (Wet bench 07)
• Fume hood 03: Solvents

Other fume hoods, such as Fume hood 04: Solvents, Fume hood 09: UV development, and Fume hood 10: e-beam development, should not be used for lift-off. For an overview of the fume hoods, click here.

Lift-off at Nanolab

Lift-off wet bench 07

Lift-off wet bench in D-3

The user manual, and contact information can be found in LabManager

Equipment		Lift-off
Purpose		Lift-off using UV resists, e.g. AZ 5214E lift-off AZ nLOF lift-off Lift-off using e-beam resists, e.g. CSAR 62 Resist strip of wafers with metal
Bath chemical		NMP (Remover 1165) / Rinse in IPA
Process parameters	Process temperature	Heating of the bath is possible. The heating has been limited to 60°C
	Ultrasonic agitation	Continuous or pulsed The power may be varied
Substrates	Substrate size	100 mm wafers 150 mm wafers
	Allowed materials	Silicon or glass wafers Film or patterning of all but Type IV (Pb, Te)
	Batch	1 - 25

Process information

Lift-off is used for lift-off using resists that are soluble in NMP (N-Methyl-Pyrrolidone), supplied in the cleanroom as "Remover 1165". Both AZ 5214E and AZ nLOF are soluble in NMP.

For information on processing of AZ nLOF, see here: Process_Flow_AZ_nLOF_2020.docx‎. For information on image reversal of AZ 5214E, see here: Process_Flow_AZ5214_rev.docx‎.