Specific Process Knowledge/Lithography/PMMA: Difference between revisions

Revision as of 14:30, 30 October 2015

Resist	Polarity	Manufacturer	Comments	Technical reports	Spinner	Thinner	Developer	Rinse	Remover	Process flows (in docx-format)
PMMA	Positive	AllResist	We have various types of PMMA in the cleanroom. Please contact Lithography for information.	MSDS PMMA File:AR-P631_679.pdf	See table here	Anisole	MIBK:IPA (1:3), IPA:H2O	IPA	acetone/1165

Spin Curves

The thickness is measured on VASE Ellipsometer using a simple Cauchy model for a transparent polymer on Si. The measurements are performed at one incidence angle (70 degrees) only. 9 points on each 4" wafer has been measured; the standard deviation thus representing the homogeinity of the film on the 4" wafers.

AllResist AR-P 672.03 (PMMA) (~ 2ml per 4" wafer) spin coated on 'Spin Coater: Manual Standard Resists, E-5, WILTID & TIGRE, 26-10-2015. Softbake 3 min @ 150 degC.
Spin Speed [rpm]	Acceleration [1/s2]	Thickness [nm]	St Dev
4000	2000	95.55	0.55
5000	2000	85.50	0.92
7000	2000	72.79	1.18

AllResist AR-P 672.03 (PMMA) diluted 1:1 in Anisole (~ 2ml per 4" wafer) spin coated on 'Spin Coater: Manual Standard Resists, E-5, WILTID & TIGRE, 26-10-2015. Softbake 3 min @ 150 degC.
Spin Speed [rpm]	Acceleration [1/s2]	Thickness [nm]	St Dev
2000	2000	51.37	0.25
3000	2000	41.97	0.24
4000	2000	36.25	0.25
5000	2000	32.42	0.30
6000	2000	30.17	0.29
7000	2000	28.76	0.43

@@ Line 26: / Line 26: @@
 | [http://www.allresist.com AllResist]
 |We have various types of PMMA in the cleanroom. Please contact [mailto:Lithography@danchip.dtu.dk Lithography] for information.
-| [[media:File:MSDS PMMA.pdf|MSDS PMMA]] [[:File:AR-P631_679.pdf]]
+| [[media:MSDS PMMA.pdf|MSDS PMMA]] [[:File:AR-P631_679.pdf]]
 |See table <u>[[Specific_Process_Knowledge/Lithography/Coaters#Coaters:_Comparison_Table|here]] </u>
 |Anisole