Specific Process Knowledge/Thermal Process/Dope with Phosphorus: Difference between revisions
No edit summary |
No edit summary |
||
| Line 17: | Line 17: | ||
====Experimental setup==== | ====Experimental setup==== | ||
''' | ''' | ||
20 boron doped device wafers (p-type) were used - Four wafers for each of the five different predeposition temperatures. In the furnace five dummy wafers were placed on each side of the device wafers. The dummy wafers nearest to the device wafers were changed in-between the runs to miniminze doping from these dummy wafers. | 20 boron doped device wafers (p-type) were used - Four wafers for each of the five different predeposition temperatures (see table below). In the furnace five dummy wafers were placed on each side of the device wafers. The dummy wafers nearest to the device wafers were changed in-between the runs to miniminze doping from these dummy wafers. | ||
{| border="1" cellspacing="1" cellpadding="2" style="text-align:center;" width="690" ||3||4||5 | {| border="1" cellspacing="1" cellpadding="2" style="text-align:center;" width="690" ||3||4||5 | ||
| Line 35: | Line 35: | ||
After the predeposition two wafers from each run were taken out to be further processed. These wafers were: 1, 2, 5, 6, 9, 10, 13, 14, 17, 18. These wafers were dipped in BHF to remove the phosphorus glass layer before the drive-in process. | After the predeposition two wafers from each run were taken out to be further processed. These wafers were: 1, 2, 5, 6, 9, 10, 13, 14, 17, 18. These wafers were dipped in BHF to remove the phosphorus glass layer before the drive-in process. | ||
The drive-in process was made in the Phosphorus Drive-in furnace (A3) for all the mentioned wafers same time. At the drive-in process a dummy wafer was placed in-between the wafers | The drive-in process was made in the Phosphorus Drive-in furnace (A3) for all the mentioned wafers at same time. At the drive-in process a dummy wafer was placed in-between the wafers that have been predeposited at different temperatures, so doping from wafer to wafer was minimized. The phosphorus drive-in was done with the process "DRY1050" which is a dry oxidation at 1050 <sup>o</sup>C for 100 minutes and 20 minutes annealing. At the oxidation the O<sub>2</sub> flow was 5 SLM, and the N<sub>2</sub> flow for annealing was 3 SLM. | ||
==== | ====Results==== | ||
''' | ''' | ||
Several measurements were done for the different | Several measurements were done for the different device waferss. After the predeposition, the thickness of the grown phosphorus glass layer was measured, and the sheet resistance and slice resistivity were measured on the same wafer after a BHF etch. | ||
{| border="2" cellpadding="2" cellspacing="1" style="text-align:center;" | {| border="2" cellpadding="2" cellspacing="1" style="text-align:center;" | ||
|+ ''' | |+ '''Measurements after phosphorus predeposition''' | ||
|- | |- | ||
! | ! | ||
| Line 51: | Line 51: | ||
! width="130" | Wafer # | ! width="130" | Wafer # | ||
! width="130" | Temperature [C] | ! width="130" | Temperature [C] | ||
! width="130" | | ! width="130" | Oxide thickness [nm] | ||
! width="130" | Refrative index | ! width="130" | Refrative index | ||
! width="150" | Sheet resistance [Ω<sub>sq</sub>] | ! width="150" | Sheet resistance [Ω<sub>sq</sub>] | ||
| Line 95: | Line 95: | ||
{| border="2" cellpadding="2" cellspacing="1" style="text-align:center;" | {| border="2" cellpadding="2" cellspacing="1" style="text-align:center;" | ||
|+ ''' | |+ '''Measurements after phosphorus drive-in''' | ||
|- | |- | ||
! | ! | ||
| Line 104: | Line 104: | ||
! width="130" | Wafer # | ! width="130" | Wafer # | ||
! width="130" | Temperature [<sup>o</sup>C] | ! width="130" | Temperature [<sup>o</sup>C] | ||
! width="130" | | ! width="130" | Oxide thickness [nm] | ||
! width="130" | Refrative index | ! width="130" | Refrative index | ||
! width="150" | Sheet resistance [Ω<sub>sq</sub>] | ! width="150" | Sheet resistance [Ω<sub>sq</sub>] | ||
| Line 144: | Line 144: | ||
| 0,165 | | 0,165 | ||
|- | |- | ||
! | ! Blank Si wafer | ||
| | | | ||
| 110,71 | | 110,71 | ||
| Line 167: | Line 167: | ||
|} | |} | ||
Looking at the | Looking at the "SIMS Measurement After Drive-in Process at 1050 <sup>o</sup>C" graph, it can be seen that the two curves "Pre-dep at 950 <sup>o</sup>C" and "Pre-dep at 1000 <sup>o</sup>C" are crossing each other, but according to the theory they should not do that. Only one wafer has been meassured, so there is not that much statistical data to verify it with. | ||
Revision as of 10:32, 21 October 2013
Feedback to this page: click here
The Phosphorus Predep furnace (A4) can be used for phosphorus predeposition of silicon wafers, resulting in N-type doping. In the furnace, the silicon wafers are positioned in a quarts boat.
Test of the Phosphorus Predep furnace
Purpose
To study the correlation between the temperature for the predeposition process and drive-in of the phosphorus doping in the Phosphorus Predep furnace (A4) at DTU Danchip.
Experimental setup
20 boron doped device wafers (p-type) were used - Four wafers for each of the five different predeposition temperatures (see table below). In the furnace five dummy wafers were placed on each side of the device wafers. The dummy wafers nearest to the device wafers were changed in-between the runs to miniminze doping from these dummy wafers.
| Run # | Temperature | Process time with POCl3 | Annealing time in N2 | Wafer # |
|---|---|---|---|---|
| 1 | 850 oC | 15 minutes | 20 miuntes | 1, 2, 3, 4 |
| 2 | 900 oC | 15 minutes | 20 miuntes | 5, 6, 7, 8 |
| 3 | 950 oC | 15 minutes | 20 miuntes | 9, 10, 11, 12 |
| 4 | 1000 oC | 15 minutes | 20 miuntes | 13, 14, 15, 16 |
| 5 | 1050 oC | 15 minutes | 20 miuntes | 17, 18, 19, 20 |
After the predeposition two wafers from each run were taken out to be further processed. These wafers were: 1, 2, 5, 6, 9, 10, 13, 14, 17, 18. These wafers were dipped in BHF to remove the phosphorus glass layer before the drive-in process.
The drive-in process was made in the Phosphorus Drive-in furnace (A3) for all the mentioned wafers at same time. At the drive-in process a dummy wafer was placed in-between the wafers that have been predeposited at different temperatures, so doping from wafer to wafer was minimized. The phosphorus drive-in was done with the process "DRY1050" which is a dry oxidation at 1050 oC for 100 minutes and 20 minutes annealing. At the oxidation the O2 flow was 5 SLM, and the N2 flow for annealing was 3 SLM.
Results
Several measurements were done for the different device waferss. After the predeposition, the thickness of the grown phosphorus glass layer was measured, and the sheet resistance and slice resistivity were measured on the same wafer after a BHF etch.
| Ellipsometer (center point only) | Four Point Probe | ||||
|---|---|---|---|---|---|
| Wafer # | Temperature [C] | Oxide thickness [nm] | Refrative index | Sheet resistance [Ωsq] | Slice Resistivity [Ωcm] |
| 3 | 850 | 27,4 | 1,4623 | 311 | 17,32 |
| 7 | 900 | 45,27 | 1,4622 | 138,5 | 7,61 |
| 11 | 950 | 61,36 | 1,4625 | 16,12 | 0,859 |
| 15 | 1000 | 80,45 | 1,4624 | 7,4 | 0,392 |
| 19 | 1050 | 119,37 | 1,4623 | 6,6 | 0,246 |
| Avg. five point on Filmtek | Four Point Probe | ||||
|---|---|---|---|---|---|
| Wafer # | Temperature [oC] | Oxide thickness [nm] | Refrative index | Sheet resistance [Ωsq] | Slice Resistivity [Ωcm] |
| 2 | 850 | 110,44 | 1,4654 | 189,7 | 13,06 |
| 6 | 900 | 116,28 | 1,4629 | 101,6 | 5,32 |
| 9 | 950 | 137,06 | 1,4604 | 10,05 | 0,527 |
| 14 | 1000 | 141,46 | 1,4651 | 4,72 | 0,216 |
| 18 | 1050 | 139,87 | 1,4659 | 3,23 | 0,165 |
| Blank Si wafer | 110,71 | 1,46286 | - | - | |
 |
 |
 |
 |
Looking at the "SIMS Measurement After Drive-in Process at 1050 oC" graph, it can be seen that the two curves "Pre-dep at 950 oC" and "Pre-dep at 1000 oC" are crossing each other, but according to the theory they should not do that. Only one wafer has been meassured, so there is not that much statistical data to verify it with.