Revision as of 14:39, 5 August 2025 view source Reet (talk \| contribs) DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers, NLAB-Nlab347-labadviser-users-35231 1,760 edits →Lessons for future thermal deposition of Zn (by Rebecca Ettlinger) ← Older edit		Latest revision as of 14:40, 5 August 2025 view source Reet (talk \| contribs) DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers, NLAB-Nlab347-labadviser-users-35231 1,760 edits →XPS of Al films to detect Zn
Line 21:		Line 21:

	[[File:Al w Zn from 20-06-2018.png\|400px\|left\|thumb\|XPS of Al film made before chamber was cleaned after Zn deposition. 10 scans per level. Zn peaks are obvious. The Zn content was up to 10 % in some layers.]]		[[File:Al w Zn from 20-06-2018.png\|400px\|left\|thumb\|XPS of Al film made before chamber was cleaned after Zn deposition. 10 scans per level. Zn peaks are obvious. The Zn content was up to 10 % in some layers.]]
	[[File:Al wo Zn from 09-07-2018.png\|400px\|~~right~~\|thumb\|XPS of Al film made after chamber was cleaned after Zn deposition and a new crucible was used for Al. 10 scans per level for Al, 30 scans per level for Zn. No Zn peaks are visible.]]		[[File:Al wo Zn from 09-07-2018.png\|400px\|left\|thumb\|XPS of Al film made after chamber was cleaned after Zn deposition and a new crucible was used for Al. 10 scans per level for Al, 30 scans per level for Zn. No Zn peaks are visible.]]