==Anneal-bond furnace (C3)== | ==Anneal-bond furnace (C3)== | ||
| Line 44: | Line 44: | ||
|- | |- | ||
!style="background:silver; color:black" align="center"|Performance | !style="background:silver; color:black" align="center"|Performance | ||
|style="background:LightGrey; color:black"|Film thickness | |style="background:LightGrey; color:black"|Film thickness and quality | ||
|style="background:WhiteSmoke; color:black"| | |style="background:WhiteSmoke; color:black"| | ||
*Dry oxide:~ 0 nm to 300 nm (it takes too long to grow thicker dry oxide layers) | *Dry oxide:~ 0 nm to 300 nm (it takes too long to grow thicker dry oxide layers) | ||
*Wet oxide: ~ 0 nm to 3 µm (23 hours wet oxidation at 1100 <sup>o</sup>C) | *Wet oxide: ~ 0 nm to 3 µm (23 hours wet oxidation at 1100 <sup>o</sup>C) | ||
* [[Specific Process Knowledge/Thermal Process/Oxidation/Breakdown voltage measurements/C3 furnace break-down voltage measurement results|Break-down voltage measurement results]] | |||
|- | |- | ||
!style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range | !style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range | ||
| Line 72: | Line 73: | ||
*Silicon wafers | *Silicon wafers | ||
*Silicon wafers with layers of silicon oxide or silicon nitride | *Silicon wafers with layers of silicon oxide or silicon nitride | ||
*Wafers from the | *Wafers from the A1, A3, B-stack, C1 and E1 stack furnaces | ||
*Wafers from PECVD4 | *Wafers and samples from PECVD4 | ||
*Wafers from PECVD3 (without any | *Wafers and samples from PECVD3 (without any metals) | ||
*Wafers from Wafer Bonder 02 ( | *Wafers from Wafer Bonder 02 | ||
*Wafers from Wafer Bonder 03 (without any metals). Use new or dedicated/clean teflon sheets in the wafer bonder | |||
|- | |- | ||
|} | |} | ||