Specific Process Knowledge/Thin film deposition/Deposition of Titanium Oxide/IBSD of TiO2

Acceptance test for TiO2 deposition:

.	Acceptance Criteria	Preliminary Results NOT ACCEPTED YET
Substrate information	50 mm SSP Si wafer 525 µm thick Supplied by Danchip	100 mm SSP Si wafer 525+-25 µm thick
Material to be deposited	TiO2 The purpose of the TiO2 is to be part of a mirror: 5 quarterwavelength pairs of SiO2 TiO2 Extra quarterwavelength layer of TiO2 5 quarterwavelength pairs of SiO2 TiO2 Design wavelength (for refractive indices and layer thicknesses): 1300nm The acceptance criteria is set up for the single SiO2 and TiO2 layers.	TiO2
Deposition thickness	147nm	~145 nm
Deposition rate	2.8 nm/min	2.39nm/min +- 0.05nm/min (one standard deviation)
Thickness uniformity	<+-1%	+-(0.7% +-0.1%)
Reproducibility	<+-1.5%	+-1.9%
Stress	<500MPa	Not measured yet