Specific Process Knowledge/Thermal Process/Annealing

From LabAdviser
Jump to navigation Jump to search

Feedback to this page: click here

This page is written by DTU Nanolab internal

Annealing

At DTU Nanolab we have five furnaces and an RTP (Rapid thermal annealing) that can be used annealing: Anneal-Oxide furnace (C1), Anneal-bond furnace (C3), Al_anneal furnace (C4), Multipurpose Anneal furnace and Jipelec RTP. Annealing normally takes place in an N2 atmosphere, or it can be done in H2 or a H2-N2 gas mixture in the Multipurpose Anneal furnace. PECVD PBSG glass is annealed in a wet atmosphere which will also oxidize the silicon substrate.

A 20 minutes N2 annealing step is also included in all recipes on the oxidation furnace, this annealing is done after the oxidation.

Comparison of the annealing furnaces

Anneal Oxide furnace (C1)

Anneal-Bond furnace (C3)

Aluminium Anneal furnace (C4)

RTP2 Jipelec

Multipurpose Anneal Furnace

General description Annealing of 4" and 6" wafers. Annealing of wafers from the LPCVD furnaces and from PECVD4. Annealing of wafers from Wafer Bonder 02 and from and PECVD4 and PECVD3. Annealing of wafers with Al and ALD deposited AL2O3 and TiO2. Rapid thermal processing, usually, annealing (RTA). Annealing, oxidation and resist pyrolysis of different samples
Annealing gas
  • N2
  • N2
  • N2
  • Ar
  • N2
  • Low vacuum is possible (min. 2/3 mbar)
  • N2
  • H2
  • H2-N2 gas mixture
  • Vacuum is possible
Process temperature
  • 700 oC - 1100 oC
  • 700 oC - 1150 oC
  • Up to 500 oC
  • 20 oC - 1200 oC
  • Max. 100 oC/s with carrier wafer or sample wafer
  • Max. 50 oC/s with SiC-coated graphite susceptor
  • Vacuum: 20 oC - 1050 o
  • No vacuum: 20 oC - 1100 oC
Substrate and Batch size
  • Small samples on a carrier wafer, horizontal
  • 1-30 50 mm wafers
  • 1-30 100 mm wafers
  • 1-30 150 mm wafers
  • Small samples on a carrier wafer, horizontal
  • 1-30 50 mm wafers
  • 1-30 100 mm wafers
  • 1-30 50 mm wafers
  • 1-30 100 mm wafers
  • Single-wafer process
  • Chips on carrier
  • 50 mm, 100 mm or 150 mm wafers
  • 1-30 50 mm, 100 mm or 150 mm wafers
  • 1-50 200 mm wafers
  • Small samples on a carrier wafer, horizontal
Allowed materials
  • All processed wafers have to be RCA cleaned, except wafers from LPCVD furnaces and PECVD4.
  • All processed wafers have to be RCA cleaned, except wafers from the Wafer Bonder 02 and from PECVD4 and PECVD3.
  • Wafers with Al
  • Silicon
  • Silicon oxides and nitrides
  • Quartz
  • Metals - ask for permisson
  • III-V materials - below 440 °C, otherwise it can lead to outgassing of toxic gases.
  • Depends on the furnace quartz ware:
    • Clean: Samples that have been RCA cleaned
    • Metal: Almost all materials, permission is needed
    • Resist pyrolysis