Deposition of ZnO is a standard, well-explored ALD process. Previously (before 2018), DEZ had its independent inlet (A1), which shared the same N2 line with the TiCl4 precursor (A2). The DEZ precursor bottle was placed in a cabinet behind the instrument in the service area, and a long pipe led the precursor to the ALD chamber. This option has been abandoned due to safety reasons. This line was very difficult to purge in case of service. The results that were obtained with the old hardware configuration now remain obsolete. Nowadays, if the user wants to deposit ZnO, in ALD-1 the diethyl zinc (DEZ) has to be mounted in the A-line. If TiCl4 is currently present it has to be exchanged with DEZ. This is a time-consuming job, that needs to be ordered and prepared in advance.

ZnO ALD deposition using DEZ and H₂O

ZnO can be deposited in the range between 100 ^oC to 225 ^oC. It is not recommended to increase the temperature above 225^oC, as the uniformity suffers due to the precursor decomposition. The maximum temperature can be 250^oC, here however the film crystal quality, crystallinity, roughness, etc. sufficiently differ from the films prepared in a lower temperature range.

All results shown on this page have been obtained using the present (from 2018) configuration. Deposition and characterization has been performed in 2021 by Evgeniy Shkondin, DTU Nanolab

ZnO recipes

Recipe: ZnO

Maximum deposition thickness: 100 nm

Temperature: 100 ^oC - 250 ^oC

	DEZ*	H₂O
Nitrogen flow	150 sccm	200 sccm
Pulse time	0.1 s	0.1 s
Purge time	5.0 s	5.0 s

This is a standard recipe of ZnO. It is suitable for coating the flat samples and structures with an aspect ratio of around up to 1:10.

Recipe: ZnOT

Maximum deposition thickness: 100 nm

Temperature: 100 ^oC - 250 ^oC

	DEZ^*	DEZ	H₂O	H₂O
Nitrogen flow	150 sccm	150 sccm	200 sccm	200 sccm
Pulse time	0.1 s	0.1 s	0.1 s	0.1 s
Purge time	0.5 s	20.0 s	0.5 s	20.0 s

This is a more complicated recipe that allows coating the sample with very high aspect ratio profiles. One SEM example is shown on one of the images below. The recipe is good for deposition on very high aspect ratio structures (with aspect ratio more than 1:20) such as deep trenches, pillars, pores etc. ZnOT recipe can also be used for deposition on polymers at low temperatures (80-120 ^oC).

DEZ is diethylzinc Zn(CH₂CH₃)₂ or ZnEt₂

Deposition characteristics

The deposition rate for ZnO depends on the temperature, see the ALD-window graph below. The uniformity, thickness, refractive index has been obtained using Ellipsometer VASE.

Deposition rate

In the graphs below the ZnO thickness vs. number of cycles for deposition temperatures between 100 ^oC and 250 ^oC presented. Results have been obtained for <100> 100 mm Si wafers with native oxide, based on ellipsometry study. The optical model used in fitting is based on Tauc-Lorentz and two Lorentz oscillators.

Deposition rate of ZnO at 100 ^oC. Substrate: Silicon 4" wafer with native oxide.
$Thickness(nm)=0.1483\cdot N+0.63$
Deposition rate of ZnO at 150 ^oC. Substrate: Silicon 4" wafer with native oxide.
$Thickness(nm)=0.1954\cdot N-2.73$
Deposition rate of ZnO at 200 ^oC. Substrate: Silicon 4" wafer with native oxide.
$Thickness(nm)=0.1842\cdot N-3.80$
Deposition rate of ZnO at 250 ^oC. Substrate: Silicon 4" wafer with native oxide.
$Thickness(nm)=0.1326\cdot N+1.13$
ALD window of ZnO

Uniformity across 100 mm wafer

Recipe "ZnO" Samples: 100mm ssp-Si

Results have been obtained for <100> 100 mm Si wafers with native oxide, based on ellipsometry study.

Temperature (°C) / Number of cycles	Deposition rate (nm/s)	Average thickness (nm)	Standard deviation	Uniformity (%)
100°C / 500cycles	0.1483	75.67	1.49	3.26
150°C / 500cycles	0.1954	95.32	1.32	2.44
200°C / 500cycles	0.1842	87.97	0.31	0.63
225°C / 500cycles	0.1622	81.09	0.45	1.07
250°C / 500cycles	0.1326	67.92	1.71	3.82

Uniformity across 100mm wafer. Deposition at 100°C
Uniformity across 100mm wafer. Deposition at 150°C
Uniformity across 100mm wafer. Deposition at 200°C
Uniformity across 100mm wafer. Deposition at 225°C
Uniformity across 100mm wafer. Deposition at 250°C

Optical functions

Results have been obtained for <100> 100 mm Si wafers with native oxide, based on ellipsometry study.

$Refractive index.$

Refractive index.
Absorption coefficient.

SEM images

Images obtained using SEM inspection.

SEM image of flat surface of ZnO. Deposition at 100°C
SEM image of flat surface of ZnO. Deposition at 150°C
SEM image of flat surface of ZnO. Deposition at 200°C
SEM image of flat surface of ZnO. Deposition at 225°C
SEM image of flat surface of ZnO. Deposition at 250°C
ZnO deposition example on high aspect ratio structures. "ZnOT" recipe was used.

ZnO XPS investigation for elemental trace analysis

Chemical composition of ZnO has been analyzed by XPS method. ZnO samples reveals chemically high quality films with no observable contaminations in temperature range 100 - 250 ^oC.

XPS survey scan of ZnO.

ZnO ALD deposition using DEZ and H2O