Specific Process Knowledge/Thermal Process/Annealing

Feedback to this page: click here

Annealing

At Danchip we have four furnaces and an RTP (Rapid thermal annealing) that can be used annealing: Anneal-Oxide furnace (C1), Anneal-bond furnace (C3), Multipurpose Anneal furnace, Noble furnace and Jipelec RTP. Annealing normally takes place in an N₂ atmosphere, or it can be done in H₂ or a H₂-N₂ gas mixture in the Multipurpose Anneal furnace. PECVD PBSG glass is annealed in a wet atmosphere which will also oxidize the silicon substrate.

A 20 minutes N₂ annealing step is also included in all recipes on the oxidation furnace, this annealing is done after the oxidation.

Comparison of the annealing furnaces

	C1: Anneal Oxide	C3: Anneal Bond	C4: Al Anneal Furnace	Noble furnace	Jipelec RTP	Multipurpose Anneal Furnace
General description	Annealing of 4" and 6" wafers. Annealing of wafers from the LPCVD furnaces and PECVD2.	Annealing of wafers from EVG-NIL and PECVD3.	Annealing of wafers with Al.	Annealing of almost all materials on silicon wafers.	Rapid thermal annealing	Annealing, oxidation and resist pyrolysis of different samples
Annealing gas	N₂	N₂	N₂	N₂	N₂ Vacuum is possible	N₂ H₂ H₂-N₂ gas mixture Vacuum is possible
Process temperature	700 ^oC - 1100 ^oC	700 ^oC - 1150 ^oC	Up to 500 ^oC	20 ^oC - 1000 ^oC	20 ^oC - 1000 ^oC Ramp up to 300 C/min	Vacuum: 20 ^oC - 1050 ^oC¨ No vacuum: 20 ^oC - 1100 ^oC
Substrate and Batch size	Small samples on a carrier wafer, horizontal 1-30 50 mm wafers 1-30 100 mm wafers 1-30 150 mm wafers	Small samples on a carrier wafer, horizontal 1-30 50 mm wafers 1-30 100 mm wafers	1-30 50 mm wafers 1-30 100 mm wafers	Small samples on a carrier wafer, horizontal 1-25 50 mm wafers 1-25 100 mm wafers, vertical and horizontal	Small samples on a carrier wafer, horizontal One 100 mm wafers on a carrier wafer	1-30 50 mm, 100 mm or 150 mm wafers 1-50 200 mm wafers Small samples on a carrier wafer, horizontal
Allowed materials	All processed wafers have to be RCA cleaned, except wafers from LPCVD furnaces and PECVD2.	All processed wafers have to be RCA cleaned, except wafers from EVG-NIL and PECVD3.	Wafers with Al	Almost all materials, permission is needed.	III-V samples Silicon wafers Some metals	Depends on the furnace quartz ware: Clean: Samples that have been RCA cleaned Metal: Almost all materials, permission is needed Resist Pyrolysis