Specific Process Knowledge/Thin film deposition/Deposition of Platinum

From LabAdviser

Feedback to this page: click here

Unless otherwise stated, this page is written by DTU Nanolab internal


Platinum deposition

Platinum can be deposited by e-beam evaporation or sputtering. In the chart below you can compare the different deposition equipment.


E-beam evaporation (Temescal) E-beam evaporation (Wordentec) Sputter deposition (Lesker) Sputter deposition (Sputter-system Metal-Oxide (PC1) and Sputter-system Metal-Nitride (PC3))
General description E-beam deposition of Pt E-beam deposition of Pt Sputter deposition of Pt Sputter deposition of Pt
Pre-clean Ar ion source none RF Ar clean RF Ar clean
Layer thickness 10Å - 600nm* 10Å - 600nm* 10Å - 600nm* 10Å - ? discuss with staff
Deposition rate 0.5Å/s to 10Å/s 0.5Å/s to 10Å/s up to 3.74 Å/s not known yet, probably similar to 'old' Lesker system
Batch size
  • Up to 4x6" wafers
  • Up to 3x8" wafers (ask for holder)
  • smaller wafers and pieces
  • 24x2" wafers or
  • 6x4" wafers or
  • 6x6" wafers
  • 1x4" wafer or
  • 1x6" wafer
  • smaller pieces
  • Up to 10x4" or 6" wafers
  • Many smaller pieces
Allowed materials
  • Silicon
  • Silicon oxide
  • Silicon (oxy)nitride
  • Photoresist
  • PMMA
  • Mylar
  • SU-8
  • Metals
  • Silicon
  • Silicon oxide
  • Silicon nitride
  • Silicon (oxy)nitride
  • Photoresist
  • PMMA
  • Mylar
  • SU-8
  • Metals
  • Carbon
 Almost any that does not outgas
Comment

* If depositing a total of more than 600 nm, please write to metal@nanolab.dtu.dk well in advance to ensure that enough material is present.

Retrieved from "https://labadviser.nanolab.dtu.dk//index.php?title=Specific_Process_Knowledge/Thin_film_deposition/Deposition_of_Platinum&oldid=47426"