Tungsten deposition

Tungsten (W) can be deposited by e-beam evaporation and sputtering. However, in case of evaporation the precess generates a lot of heat (despite water cooling), and this means the pressure rises as the chamber is baking out. It is therefore not easy to deposit films much thicker than 50-60 nm. In the Temescal we stopped the deposition every 20 nm to let the pressure drop. Also, the rate needs to be low, to avoid overheating. Talk to staff when you want to deposit W (write to thinfilm@nanolab.dtu.dk). Sputtering can be used without any sufficient issues. In the chart below you can compare the deposition equipment.

Sputtering of W

Sputtering of Tungsten in the Sputter Coater 3

	E-beam evaporation (Temescal)	Sputter-system (Lesker)	Sputter deposition ((Sputter-system Metal-Oxide (PC1) and Sputter-system Metal-Nitride (PC3)) )	Sputter coater (Sputter coater 03)
General description	E-beam evaporation of W	DC Sputtering of W	DC and HiPIMS Sputtering of W	DC Sputtering of W
Pre-clean	Ar ion beam	None	RF bias on a substrate	None
Layer thickness	10Å to 20nm*	10Å to 600nm	10Å to 600nm	10Å to 600nm
Deposition rate	0.5 Å/s to 1 Å/s	about 1 Å/s	about 1 Å/s	about 1 Å/s
Batch size	Up to 4x6" wafers Up to 3x8" wafers (ask for holder) small pieces	Up to 1x4" wafers Up to 1x6" wafer small pieces	Up to 1x4" wafers Up to 1x6" wafer small pieces	Up to 1x4" wafers Up to 1x6" wafer small pieces
Allowed materials	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar SU-8 Metals	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar SU-8 Metals	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar SU-8 Metals	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar SU-8 Metals
Comments	Substrate gets hot during deposition (for a 60 nm film it rose above 123 C) Wait for low base pressure (3-5 10^-7 Torr)	Deposition rate is 0.107 nm/s for 150W and 3mTorr (Src3, DC)	Deposition rate is 0.124 nm/s for 140W and 3mTorr (PC3, Src3 DC), (0.04 nm/s using HiPIMS - PC3, Src3)	Deposition rate is 0.083 nm/s for 150W and 3mTorr

* For thicknesses above 20 nm talk to staff (write to thinfilm@nanolab.dtu.dk), as the heat and subsequent pressure rise means the deposition needs to be carried out in steps.