Specific Process Knowledge/Thin film deposition/ALD Picosun R200/ALD multilayers

This page describes non standart recipes including multilayers structures.

Low temperature deposition of Al₂O₃

Recipe: Al2O3 LT

Temperature: 80-150 ^oC

	TMA	H2O
Nitrogen flow	150 sccm	200 sccm
Pulse time	0.1 s	0.2 s
Purge time	5.0 s	10.0 s

Deposition rate: 0.089 nm/cycle (@120 ^oC)

Al2O3 deposition at 120 oC

Deposition conditions at 120 oC for Al2O3 LT recipe Number of cycles Thickness (nm) Uniformity across 100mm Si substrate (%) Standard deviation error Refractive index @ 632.8 nm 250 19.58 2.23 0.35 1.66 500 37.94 2.09 0.60 1.65 750 56.52 1.85 0.81 1.65 1000 75.91 1.49 0.59 1.65

%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%

Low temperature deposition of TiO₂

Recipe: TiO2 LT

Temperature: 80-150 ^oC

	TiCl4	H2O
Nitrogen flow	150 sccm	200 sccm
Pulse time	0.2 s	0.2 s
Purge time	10.0 s	15.0 s

Deposition rate: 0.048 nm/cycle (@ 120 ^oC)

Low temperature grown multilayers on flat surfaces

Recipe: EMA01

Recipe: EMA02

Recipe: EMA03

Recipe: EMA04

Temperature: 120 ^oC

Al₂O₃/TiO₂ multilayers on high aspect ratio structures

Recipe: Multi T

Temperature: 150 ^oC

• 
  Al₂O₃/TiO₂ multilayers grown on silicon trenches.

Evgeniy Shkondin, DTU Danchip, 2014-2016.