Specific Process Knowledge/Etch/DRIE-Pegasus/Pegasus-4/SiO2 Etch/Cr mask: Difference between revisions

From LabAdviser
← Older editNewer edit →
VisualWikitext
Bghe (talk | contribs)
DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers, Bureaucrats, Administrators
7,301 edits
Bghe (talk | contribs)
DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers, Bureaucrats, Administrators
7,301 edits
Line 86: Line 86:
{| border="2" cellspacing="2" cellpadding="3"  
{| border="2" cellspacing="2" cellpadding="3"  
!Recipe settings
!Recipe settings
!Comments
!SEM gallery
!SEM gallery
|-
|-
Line 100: Line 101:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on full wafer 6 min etch" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on full wafer 6 min etch" perrow="6" widths="200px" heights="150px">


Line 122: Line 124:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch" perrow="6" widths="200px" heights="150px">


Line 143: Line 146:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm" perrow="6" widths="200px" heights="150px">
File:C10025_03__11.jpg
File:C10025_03__11.jpg
Line 164: Line 168:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, O2:5sccm" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, O2:5sccm" perrow="6" widths="200px" heights="150px">
File:C10026_03__05.jpg
File:C10026_03__05.jpg
Line 185: Line 190:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr" perrow="6" widths="200px" heights="150px">
File:C10082_11.jpg
File:C10082_11.jpg
Line 209: Line 215:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr; platen power 150W, coil power:1200W" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr; platen power 150W, coil power:1200W" perrow="6" widths="200px" heights="150px">
File:C10084_15.jpg
File:C10084_15.jpg
Line 230: Line 237:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W" perrow="6" widths="200px" heights="150px">
File:C10093_03__11.jpg
File:C10093_03__11.jpg
Line 251: Line 259:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W" perrow="7" widths="200px" heights="150px">
File:C10101_03__12.jpg
File:C10101_03__12.jpg
Line 273: Line 282:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
File:C10102_03__05.jpg
File:C10102_03__05.jpg
Line 294: Line 304:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
File:C10110_04.jpg
File:C10110_04.jpg
Line 314: Line 325:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
File:C10119_01.jpg
File:C10119_01.jpg
Line 335: Line 347:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier '''14 min etch''' (PLEASE DO NOT REPEAT THIS LONG TIME), H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier '''14 min etch''' (PLEASE DO NOT REPEAT THIS LONG TIME), H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
File:C10160_02.jpg
File:C10160_02.jpg
Line 357: Line 370:
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
*PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier '''10 min etch''', H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier '''10 min etch''', H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W" perrow="6" widths="200px" heights="150px">
File:C10161_01.jpg
File:C10161_01.jpg
Line 379: Line 393:
*'''Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A''''  
*'''Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A''''  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:1200W" perrow="7" widths="200px" heights="150px">
File:C10184_01.jpg
File:C10184_01.jpg
Line 406: Line 421:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:2500W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:2500W" perrow="7" widths="200px" heights="150px">
File:C10381_04.jpg
File:C10381_04.jpg
Line 425: Line 441:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:225sccm O2:0sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:225sccm O2:0sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W" perrow="7" widths="200px" heights="150px">
File:C10393_04.jpg
File:C10393_04.jpg
Line 447: Line 464:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W" perrow="7" widths="200px" heights="150px">
File:C10399_01.jpg
File:C10399_01.jpg
Line 468: Line 486:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0" perrow="7" widths="200px" heights="150px">
<gallery caption="SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0" perrow="7" widths="200px" heights="150px">
File:C10576_02.jpg
File:C10576_02.jpg
Line 491: Line 510:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption=" C10751: SiO2 etch with Cr mask on wafer piece on Si carrier 20 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 50W, coil power:600W" perrow="7" widths="200px" heights="150px">
<gallery caption=" C10751: SiO2 etch with Cr mask on wafer piece on Si carrier 20 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 50W, coil power:600W" perrow="7" widths="200px" heights="150px">
File:C10751_02.jpg
File:C10751_02.jpg
Line 511: Line 531:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption=" C10752: SiO2 etch with Cr mask on wafer piece on Si carrier 30 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px">
<gallery caption=" C10752: SiO2 etch with Cr mask on wafer piece on Si carrier 30 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px">
File:C10752_01.jpg
File:C10752_01.jpg
Line 532: Line 553:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption=" C10834: SiO2 etch with Cr mask on wafer piece on Si carrier 45 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px">
<gallery caption=" C10834: SiO2 etch with Cr mask on wafer piece on Si carrier 45 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px">
File:C10834_12.jpg
File:C10834_12.jpg
Line 558: Line 580:
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'  
|
|
|text
<gallery caption=" C10844: SiO2 etch with Cr mask on wafer piece on Si carrier 50 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 20W, coil power:300W" perrow="6" widths="200px" heights="150px">
<gallery caption=" C10844: SiO2 etch with Cr mask on wafer piece on Si carrier 50 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 20W, coil power:300W" perrow="6" widths="200px" heights="150px">
File:C10844_02.jpg
File:C10844_02.jpg

Revision as of 14:39, 6 February 2024

Feedback to this page: click here
Unless otherwise stated, all content in this section was done by Berit Herstrøm, DTU Nanolab

SiO2 trench etching with Cr mask

Start parameters, variations noted in the gallery headline Recipe name: no 10 with lower platen power
Coil Power [W] 2500
Platen Power [W] 200
Platen temperature [oC] 20
H2 flow [sccm] 25.6
C4F8 flow [sccm] 25.6
He flow [sccm] 448.7
Pressure Fully open APC valve (8-9 mTorr)
Electromagnetic coils (EM) 'outer coil' / 'inner coil' '2 A' / '30 A' (PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN)
  • 100 nm Cr mask etched in ICP metal with 500nm DUV neg resist (NUV 2300-0.5) and 65 nm barc.
Cr mask before SiO2 etch 800 nm pitch 50% duty cycle. The The Cr linewidth is clearly less than designed


Results

Temporary conclusions on how the process parameters affect the results in this study: What process parameters affect the results?
  • Going from full wafer to small piece on Si carrier:
    • Seemed to give more sidewall passivation
  • Platen power: lowering the platen power gives
    • more sidewall passivation
    • lower etch rate
    • Less trenching
  • Removing the H2 gave:
    • less sidewall passivation
  • Adding O2 gave:
    • less sidewall passivation
  • Process pressure/total gasflow rate
    • Reducing total gasflow rate which reduced the pressur inside the chamber gave:
      • less sidewall passivation
      • Reduced the CD (Critical Dimensions)
  • Coil power: Reducing coil power
    • less CD loss
    • more sidewall passivation
  • Increasing process time:
    • less sidewall passivation
    • more sidewall bow
    • CD loss due to larger mask faceting
  • Sidewall passivation↑
    • Sample size↓
    • Platen power↓
    • Coil power↓
    • H2 flow↑
    • O2 flow↓
    • Total gas flow rate/pressure↑

Profile SEM images

Recipe settings Comments SEM gallery
  • On 6" wafer
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:25.6
  • C4F8 flow [sccm]: 25.6
  • He flow [sccm]:448.7
  • Pressure:Fully open APC valve (8-9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on full wafer 6 min etch
  • Piece on Si carrier
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:25.6
  • C4F8 flow [sccm]: 25.6
  • He flow [sccm]:448.7
  • Pressure:Fully open APC valve (8-9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • C4F8 flow [sccm]: 25.6
  • He flow [sccm]:448.7
  • Pressure:Fully open APC valve (8-9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 5
  • C4F8 flow [sccm]: 25.6
  • He flow [sccm]:448.7
  • Pressure:Fully open APC valve (8-9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, O2:5sccm
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 0
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:225
  • Pressure:Fully open APC valve (3.35 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr
  • Coil Power [W]:1200
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 0
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:225
  • Pressure:Fully open APC valve (3.35 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr; platen power 150W, coil power:1200W
  • Coil Power [W]:1200
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:215
  • Pressure:Fully open APC valve (3.35 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W
  • Coil Power [W]:1200
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.35 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W
  • Coil Power [W]:1800
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:215
  • Pressure:Fully open APC valve (3.35 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
  • Coil Power [W]:1800
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.6 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
  • pitch 800 nm Top 461 nm @edge 437 nm bottom 402 nm height 916 nm height from edge 827 nm Cr left 83.5 nm selectivity 55.5
    pitch 800 nm
    Top 461 nm
    @edge 437 nm
    bottom 402 nm
    height 916 nm
    height from edge 827 nm
    Cr left 83.5 nm
    selectivity 55.5
  • 156 nm/min
    156 nm/min
  • Coil Power [W]:1200
  • Platen Power [W]: 100
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.6 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W
  • pitch 800 nm Top 444 nm bottom 374 nm height 718 nm Cr left 85 nm selectivity 48
    pitch 800 nm
    Top 444 nm
    bottom 374 nm
    height 718 nm
    Cr left 85 nm
    selectivity 48
  • Coil Power [W]:1200
  • Platen Power [W]: 100
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.6 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch (PLEASE DO NOT REPEAT THIS LONG TIME), H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W
  • Etch on none patterned wafer, Uniformity: +- 6.4%
    Etch on none patterned wafer, Uniformity: +- 6.4%
  • Coil Power [W]:1800
  • Platen Power [W]: 150
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.6 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'2 A' / '30 A'
  • PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 10 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
  • Coil Power [W]:1200
  • Platen Power [W]: 100
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:1200W
  • Etch on none patterned wafer, Uniformity: +-1.7%
    Etch on none patterned wafer, Uniformity: +-1.7%
  • tilt 30 degrees
    tilt 30 degrees
  • tilt 30 degrees
    tilt 30 degrees
  • tilt 20 degrees
    tilt 20 degrees
  • tilt 20 degrees
    tilt 20 degrees
  • Coil Power [W]:2500
  • Platen Power [W]: 100
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:2500W
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 0
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:225
  • Pressure:Fully open APC valve (3.9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:225sccm O2:0sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W
  • 14 min
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 20
  • C4F8 flow [sccm]: 13.0
  • He flow [sccm]:205
  • Pressure:Fully open APC valve (3.9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 200W, coil power:2500W
  • Back to start setting without EM coils - 14 min
  • Coil Power [W]:2500
  • Platen Power [W]: 200
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:25.6
  • O2 flow [sccm]: 0
  • C4F8 flow [sccm]: 25.6
  • He flow [sccm]:448.7
  • Pressure:Fully open APC valve (8-9 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0
  • Coil Power [W]:600
  • Platen Power [W]: 50
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 6.5
  • He flow [sccm]:100
  • Pressure:Fully open APC valve (<2 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • C10751: SiO2 etch with Cr mask on wafer piece on Si carrier 20 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 50W, coil power:600W
  • Coil Power [W]:300
  • Platen Power [W]: 25
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 6.5
  • He flow [sccm]:100
  • Pressure:Fully open APC valve (<2 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • C10752: SiO2 etch with Cr mask on wafer piece on Si carrier 30 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W
  • 45 min
  • Coil Power [W]:300
  • Platen Power [W]: 25
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 6.5
  • He flow [sccm]:100
  • Pressure:Fully open APC valve (<2 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • C10834: SiO2 etch with Cr mask on wafer piece on Si carrier 45 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W
  • Coil Power [W]:300
  • Platen Power [W]: 20
  • Platen temperature [oC]: 20
  • H2 flow [sccm]:0
  • O2 flow [sccm]: 10
  • C4F8 flow [sccm]: 6.5
  • He flow [sccm]:100
  • Pressure:Fully open APC valve (<2 mTorr)
  • Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A'
 text
  • C10844: SiO2 etch with Cr mask on wafer piece on Si carrier 50 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 20W, coil power:300W