[[File:SiO2 etch uniformity DOE3_10.JPG|400px|thumb|left|Etched for 3min56s, average etch rate: 250 nm/min +- 2.9% ]] | [[File:SiO2 etch uniformity DOE3_10.JPG|400px|thumb|left|Etched for 3min56s, average etch rate: 250 nm/min +- 2.9% ]] | ||
[[File:Contour Plot Y31 EM_02_30 white to blue.jpg|400px|thumb|left|Etched with EM:02/30 for 2min, average etch rate: 275 nm/min +- 4.5%. The electro magnets changed the uniformity pattern and made it a bit worse ]] | [[File:Contour Plot Y31 EM_02_30 white to blue.jpg|400px|thumb|left|Etched with EM:02/30 for 2min, average etch rate: 275 nm/min +- 4.5%. The electro magnets changed the uniformity pattern and made it a bit worse ]] | ||