Specific Process Knowledge/Etch/DRIE-Pegasus/Pegasus-2/ORE with Al2O3 mask: Difference between revisions
| Line 19: | Line 19: | ||
Using patterned samples of 1 μm pillars with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 32nm of Al<sub>2</sub>O<sub>3</sub> were still intact. | Using patterned samples of 1 μm pillars with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 32nm of Al<sub>2</sub>O<sub>3</sub> were still intact. | ||
<br clear="all" /> | <br clear="all" /> | ||
[[File:compare pillars.png| | [[File:compare pillars.png|400px|left|thumb|'''''Pillars with different etching times.''''']] | ||
{| border="1" style="text-align: center; width: 650px; height: 200px" | {| border="1" style="text-align: center; width: 650px; height: 200px" | ||
|+ 1μm Pillar recipe from March 2022 - #244 = 122 min | |+ 1μm Pillar recipe from March 2022 - #244 = 122 min | ||
| Line 39: | Line 39: | ||
=== Holes === | === Holes === | ||
Using patterned samples of 1 μm holes with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 28nm of Al<sub>2</sub>O<sub>3</sub> were still intact. | Using patterned samples of 1 μm holes with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 28nm of Al<sub>2</sub>O<sub>3</sub> were still intact. | ||
[[File:holes 17 e 10 um.png| | [[File:holes 17 e 10 um.png|400px|left|thumb|'''''Holes profile.''''']] | ||
{| border="1" style="text-align: center; width: 900px; height: 200px" | {| border="1" style="text-align: center; width: 900px; height: 200px" | ||
|+ 1μm holes recipe from March 2022 | |+ 1μm holes recipe from March 2022 | ||