=<span style="color:#FF0000">This work has been done on PECVD2. PECVD2 has been decomissioned but we keep this information because we expect PECVD3 and PECVD4 to behave similar</span>= | =<span style="color:#FF0000">This work has been done on PECVD2. PECVD2 has been decomissioned but we keep this information because we expect PECVD3 and PECVD4 to behave similar</span>= |
Revision as of 08:38, 5 October 2020
Feedback to this page: click here
This work has been done on PECVD2. PECVD2 has been decomissioned but we keep this information because we expect PECVD3 and PECVD4 to behave similar
Boron-doping by use of BSG glass deposited in PECVD2
Results from Joachim Dahl Thomsen, Nanotech, 2014
Recipe
Recipe name | SiH4 flow [sccm] | N2O flow [sccm] | N2 flow [sccm] | B2H6 flow [sccm] | PH3 flow [sccm] | Pressure [mTorr] | Power [W] | Description |
1PBSG | 17 | 1600 | 0 | 120, 130, 140, 160, 240 | 0 | 400 | 380 | BSG glass for driving in boron in Silicon |
5 tests were made where only the B2H6 flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in 440 nm Oxide. The wafers were annealed in Anneal Oxide Furnace (C1) at 1000°C for 85 min to drive in the boron and the oxide was subsequently etched in BHF.
The wafers were then analyzed by SIMS and the results are shown in the figure below:
Boron-doping by use of BSG glass deposited in PECVD2
Results from Trine Holm Christensen, Space, Feb. 2015
Recipe
Recipe name | SiH4 flow [sccm] | N2O flow [sccm] | N2 flow [sccm] | B2H6 flow [sccm] | PH3 flow [sccm] | Pressure [mTorr] | Power [W] | Description |
1PBSG | 17 | 1600 | 0 | 120, 130, 140 | 0 | 400 | 380 | BSG glass for driving in boron in Silicon |
3 tests were made where only the B2H6 flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in approximately 400nm Oxide.
The wafers were going through several annealing and oxidation step:
The total thermal budget for the wafers:
Anneal in Furnace (C1): ANN1000, 30 min in N2, strip of oxide in a 25 min BHF etch.
Wet oxidation in Furnace (C1): WET1050, 30 min, no further anneal
Anneal in Furnace (C1): ANN950, 60 min in N2
The wafers were then analyzed by SIMS and the results are shown in the figure below:
Measured peak concentrations and sheet resistances:
Wafer | Peak Concentration
[atoms/cm3] |
Sheet Resistance
[Ω/sq] |
BSG120 | 1.75*1019 | 56.4 |
BSG130 | 2.44*1019 | 36.2 |
BSG140 | 2.36*1019 | 40.3 |