Grains in a sputtered TiW film

TiW films were deposited by sputtering in the Wordentec. AFM pictures show how the surface roughness is dependent on the process parameters.

For the sputter process, the power and argon pressure can be set to different values. Depending on the process parameters, the deposited layers will have different characteristics: the roughness, grain size and uniformity may be different.

Power 150 W, pressure 1*10^-3 mbar

With use of the settings 150W and 1*10^-3 mbar, a surface with low roughness is deposited.

Measurement done September 2008, KNIL.

@@ Line 1: / Line 1: @@
-=<span style="background:#FF2800">THIS PAGE IS UNDER CONSTRUCTION</span>=
+'''Feedback to this page''': '''[mailto:labadviser@nanolab.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.nanolab.dtu.dk/index.php/Specific_Process_Knowledge/Thin_film_deposition/Deposition_of_TiW/Sputtering_of_TiW_in_Wordentec/Grain_size_and_uniformity_of_TiW_layers click here]'''
+==Grains in a sputtered TiW film==
+TiW films were deposited by sputtering in the Wordentec. AFM pictures show how the surface roughness is dependent on the process parameters.
+For the sputter process, the power and argon pressure can be set to different values. Depending on the process parameters, the deposited layers will have different characteristics: the roughness, grain size and uniformity may be different.
+'''Power 150 W, pressure 1*10<sup>-3</sup> mbar'''
+With use of the settings 150W and 1*10<sup>-3</sup> mbar, a surface with low roughness is deposited.
+[[Image:Tiw 150W 0 001 nr2.jpg|480x480px|center|thumb|AFM picture of sputter deposited TiW. Used settings: 150W and 1*10<sup>-3</sup> mbar.]]
+''Measurement done September 2008, KNIL.''