Specific Process Knowledge/Etch/Aluminum Oxide/Al2O3 Etch using HF: Difference between revisions
| Line 10: | Line 10: | ||
Si samples with about 100 nm of [[Specific_Process_Knowledge/Thin_film_deposition/ALD_Picosun_R200|ALD]] deposited Al<sub>2</sub>O<sub>3</sub> (1000 cycles at 300<sup>o</sup>C) has been etched in different HF concentrations. After the etching, the thickness of the Al<sub>2</sub>O<sub>3</sub> layer has been measured, and the thickness as function of time has been plotted as shown in the graph below. | Si samples with about 100 nm of [[Specific_Process_Knowledge/Thin_film_deposition/ALD_Picosun_R200|ALD]] deposited Al<sub>2</sub>O<sub>3</sub> (1000 cycles at 300<sup>o</sup>C) has been etched in different HF concentrations. After the etching, the thickness of the Al<sub>2</sub>O<sub>3</sub> layer has been measured, and the thickness as function of time has been plotted as shown in the graph below. | ||
<gallery caption="attempt to dissolve Al<sub>2</sub>O<sub>3</sub> with HF." widths="500px" heights="500px | <gallery caption="attempt to dissolve Al<sub>2</sub>O<sub>3</sub> with HF." widths="500px" heights="500px"> | ||
image:AL203_Hf_etch.jpg | image:AL203_Hf_etch.jpg | ||
</gallery> | </gallery> | ||