Etching Al₂O₃ can be done both chemically and by dry etching. We have not tested a chemical etch but a possibility could be to use a developer. This will be selective to most materials not containing Al. Do expect a slow and isotropic etch rate of about 1-2 nm/min. We have done some test of Al2O3 in dry etching. It has been mostly tested in the III-V ICP. Please see links below.

@@ Line 1: / Line 1: @@
 '''Feedback to this page''': '''[mailto:labadviser@danchip.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.danchip.dtu.dk/index.php/Specific_Process_Knowledge/Etch/Aluminum_Oxide click here]'''
-Etching Al2O3 can be done both chemically and by dry etching. We have not tested a chemical etch but a possibility could be to use a developer. This will be selective to most materials not containing Al. Do expect a slow and isotropic etch rate of about 1-2 nm/min. We have done some test of Al2O3 in dry etching. It has been mostly tested in the III-V ICP. Please see links below.
+Etching Al<sub>2</sub>O<sub>3</sub> can be done both chemically and by dry etching. We have not tested a chemical etch but a possibility could be to use a developer. This will be selective to most materials not containing Al. Do expect a slow and isotropic etch rate of about 1-2 nm/min. We have done some test of Al2O3 in dry etching. It has been mostly tested in the III-V ICP. Please see links below.
 *[[/Al2O3 Etch with ICP Metal|Al2O3 etch using ICP metal]]
 *[[/Al2O3 Etch with III-V ICP|Al2O3 etch using III-V ICP]]