==InP etching June 2018== | |||
===With InP piece on Si carrier=== | |||
InP piece patterned with SiO2. The pice was etched on topof a Siwafer with out bonding. The InP etch was used. | |||
<gallery> | |||
caption="Result of InP etching." widths="300px" heights="200px" perrow="5"> | |||
Image:S1_00.jpg | |||
Image:S1_30dg_01.jpg | |||
Image:S1_30dg_02.jpg | |||
Image:S1_30dg_03.jpg | |||
Image:S1_30dg_04.jpg | |||
Image:S1_30dg_05.jpg | |||
Image:S1_30dg_06.jpg | |||
Image:S1_30dg_07.jpg | |||
Image:S1_30dg_08.jpg | |||
Image:S1_30dg_09.jpg | |||
Image:S1_30dg_10.jpg | |||
Image:S1_30dg_midt_11.jpg | |||
Image:S1_30dg_midt_12.jpg | |||
Image:S1_30dg_midt_13.jpg | |||
Image:S1_30dg_midt_14.jpg | |||
</gallery> | </gallery> | ||
Revision as of 12:09, 19 June 2018
Feedback to this page: click here
InP/InGaAsP/InGaAs etch
Unselective etch for large sized features and small aspect ratios by David Larsson, DTU Photonics, 2011
| Recipe | InP Etch 1/InP Precond 1 |
| Cl2 flow | 20 sccm |
| N2 flow | 40 sccm |
| Ar flow | 10 sccm |
| Platen power | 100 W |
| Coil power | 500 W |
| Pressure | 2 mTorr |
| Platen chiller temperature | 180 oC |
| Results (InP Etch 1) | |
| Etch rate | 500-600 nm/min |
| Sidewall angle | 86-87 o |
| Selectivity (InP:SiO2, InP:HSQ) | 50:1 |
- Result of InP etching. David Larsson, DTU Photonics, 2011
-
-
InP etching June 2018
With InP piece on Si carrier
InP piece patterned with SiO2. The pice was etched on topof a Siwafer with out bonding. The InP etch was used.