XPS measurements shows that at temperaturs below 120 <sup>o</sup>C the TiO<sub>2</sub> layer will be contaminated with about 1-3 % chlorine molecules from the TiCl<sub>4</sub> precursor. This can be seen as small white dots in SEM images of the anatase TiO<sub>2</sub> layers. | XPS measurements shows that at temperaturs below 120 <sup>o</sup>C the TiO<sub>2</sub> layer will be contaminated with about 1-3 % chlorine molecules from the TiCl<sub>4</sub> precursor. This can be seen as small white dots in SEM images of the anatase TiO<sub>2</sub> layers. | ||
===TiO<sub>2</sub> standard recipe=== | ===TiO<sub>2</sub> standard recipe=== | ||
| Line 37: | Line 38: | ||
|- | |- | ||
|} | |} | ||
===TiO<sub>2</sub> deposition rates=== | |||
In the graphs below the TiO<sub>2</sub> thickness as function of the number of cycles for deposition temperatures between 150 <sup>o</sup>C and 350 <sup>o</sup>C can be seen. From the equations the number of cycles required for a certain thickess can be calculated. | In the graphs below the TiO<sub>2</sub> thickness as function of the number of cycles for deposition temperatures between 150 <sup>o</sup>C and 350 <sup>o</sup>C can be seen. From the equations the number of cycles required for a certain thickess can be calculated. | ||
===TiO<sub>2</sub> results=== | ===TiO<sub>2</sub> results=== | ||