Specific Process Knowledge/Lithography/mrEBL6000: Difference between revisions

From LabAdviser
Tigre (talk | contribs)
No edit summary
Tigre (talk | contribs)
No edit summary
Line 29: Line 29:
|
|
|[[media:Process_Flow_mrEBL6000.docx‎|Process_Flow_mrEBL6000.docx‎]]
|[[media:Process_Flow_mrEBL6000.docx‎|Process_Flow_mrEBL6000.docx‎]]
|}
[[File:SpinCurveMrEBL6000.jpg|right|600px]]
The thickness is measured on VASE Ellipsometer using a simple Cauchy model for a transparent polymer on Si. The measurements are performed at one incidence angle (70 degrees) only. 9 points on each 4" wafer has been measured; the standard deviation thus representing the homogeinity of the film on the 4" wafers.
{|border="1" cellspacing="0" cellpadding="3" style="text-align:left;"  style="width: 40%"
|-
|-
|-style="background:Black; color:White"
!colspan="7"|MicroResist mr EBL 6000 spinning on Spin Coater: Manual LabSpin A-5, TIGRE, 14-07-2014. Softbake 3 min @ 110 degC.
|-
|-
|-style="background:WhiteSmoke; color:black"
!Spin Speed [rpm]
!Acceleration [1/s2]
!Thickness [nm]
!St Dev
|-
|-
|-style="background:WhiteSmoke; color:black"
|2000
|2000
|
|
|-
|-
|-style="background:WhiteSmoke; color:black"
|3000
|2000
|
|
|-
|-
|-style="background:WhiteSmoke; color:black"
|4000
|2000
|
|
|-
|-
|-style="background:WhiteSmoke; color:black"
|5000
|2000
|
|
|-
|-
|-style="background:WhiteSmoker; color:black"
|6000
|2000
|
|
|-
|}
|}

Revision as of 12:47, 14 July 2014

Resist Polarity Manufacturer Comments Technical reports Spinner Developer Rinse Remover Process flows (in docx-format)
mr EBL 6000 Positive MicroResist Standard negative resist mrEBL6000 processing Guidelines.pdf‎ Manual Spinner 1 (Laurell), Spin Coater Labspin mr DEV IPA Process_Flow_mrEBL6000.docx‎


The thickness is measured on VASE Ellipsometer using a simple Cauchy model for a transparent polymer on Si. The measurements are performed at one incidence angle (70 degrees) only. 9 points on each 4" wafer has been measured; the standard deviation thus representing the homogeinity of the film on the 4" wafers.


MicroResist mr EBL 6000 spinning on Spin Coater: Manual LabSpin A-5, TIGRE, 14-07-2014. Softbake 3 min @ 110 degC.
Spin Speed [rpm] Acceleration [1/s2] Thickness [nm] St Dev
2000 2000
3000 2000
4000 2000
5000 2000
6000 2000