Specific Process Knowledge/Thin film deposition/Deposition of Nickel: Difference between revisions
| Line 12: | Line 12: | ||
! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Wordentec|Wordentec]]) | ! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Wordentec|Wordentec]]) | ||
! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Multisource PVD|PVD co-sputter/evaporation]]) | ! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Multisource PVD|PVD co-sputter/evaporation]]) | ||
! Electroplating ([[Specific Process Knowledge/Thin film deposition/Electroplating-Ni|Electroplating-Ni | ! Electroplating ([[Specific Process Knowledge/Thin film deposition/Electroplating-Ni|Electroplating-Ni]]) | ||
|- | |- | ||
| Batch size | | Batch size | ||
Revision as of 15:00, 8 May 2013
Feedback to this page: click here
Nickel deposition
Nickel can be deposited by e-beam evaporation. In the chart below you can compare the different deposition equipment.
| E-beam evaporation (Alcatel) | E-beam evaporation (Wordentec) | E-beam evaporation (PVD co-sputter/evaporation) | Electroplating (Electroplating-Ni) | |
|---|---|---|---|---|
| Batch size |
|
|
|
|
| Pre-clean | RF Ar clean | RF Ar clean | RF Ar clean | None |
| Layer thickness | 10Å to 1µm | 10Å to 1 µm | 10Å to 1000 Å | A few µm to 1400 µm |
| Deposition rate | 2Å/s to 15Å/s | 10Å/s to 15Å/s | About 1Å/s | About 10 to 250 Å/s |
| Comment | Only very thin layers (up to 100nm). | Sample must be compatible with plating bath. Seed metal necessary. |