Specific Process Knowledge/Lithography/EBeamLithography/JEOL 9500 User Guide

Purpose, location and technical specifications

Type and location of machine

The JEOL JBX-9500FS electron beam lithography system is a spot electron beam lithography system designed for use in writing patterns (10 nm - 1 µm) in electron sensitive resists. The JEOL JBX-9500FS was purchased in 2012 and is installed in E-1 and E-2 at DTU Nanolabv. The main console of the e-beam writer is installed in E-2 which is a class 10 (ISO 4) cleanroom with tight temperature and moisture control. The computer controlling the e-beam (EWS/9500) and the computer supporting the conversion of e-beam files are located in E-1 which is a class 100 (ISO 5) cleanroom.

Authorization

• Only authorized users are allowed to use this machine. You require at least 4 training sessions to be authorized.
• No unauthorized users are allowed into the e-beam room E-2 unless they are accompanied with a member of DTU Nanolab staff.
• In E-2, all users must keep within the area between the front side of the machine and the table with the pre-aligner setup. Only JEOL staff or DTU Nanolab staff may access the backside of the machine.
• No users, not even authorised users, are allowed to load a substrate into the autoloader (robot loader).
• After your exposure, fully trained users can unload their cassettes from the autoloader and unmount their substrates .
• If you are prohibited to unmount your substrates before another user requires the cassette, you must accept that either the next user or DTU Nanolab personel unmount your substrates.

Any violation of the above rules will result in eviction from the cleanroom.

Original JEOL Manual

The original JEOL manual for the e-beam writer JEOL JBX-9500FS is located on the O-drive: O:\CleanroomDrive\_Equipment\E-beam

Techical Specification

The system can be characterized as follows:

• The spot beam for electron beam writing is generated by a ZrO/W emitter and a four-stage electron beam focusing lens system, see illustration below.
• Electron-beam scanning speeds, f, up to 100 MHz are available (which is maximum scan speed).
• The acceleration voltage is 100 kV.
• The e-beam writer can pattern structures with a minimum resolution of 12 nm.
• The maximum field-size without stitching is 1000µm x 1000µm.
• The machine has cassettes that can contain either 6 wafers of 2” in size, 2 or 3 wafers of 4” in size, 1 wafer of 6” in size, 1 wafer of 8” in size, 4 chips of different sizes(slot sizes 4 mm, 8 mm, 12 mm, and 20 mm)

Rough estimation of exposure time

Go to top of this page

Pattern writing using the e-beam writer is implemented on a wafer or chip which has been coated with an electron sensitive resist. Both positive and negative types of resists for pattern writing can be used. In either case, the resist sensitivity Q (C/cm2) is a function of the beam current, I (A), the pattern writing area, A (cm2), and the pattern writing time t (s), as given below:

Q = It/A

The e-beam scanning frequency f (Hz) is a function of the e-beam scanning step, p (shot step), as shown below:

f = I /(Qp2)

The e-beam writer has scan speeds up to 100 MHz available. The dose, Q, shot step, p, and current, I, is chosen to meet the requirement of the pattern to be written, the writing time available, and also to meet the requirement f < 100MHz.

Based on the equations above, a rough estimate of the exposure time is easily calcualted. In the second sheet of the e-beam logbook, a simple program for calculating the scan speed frequency and an estimation of the exposure time can be found. Note, that the actual writing time will exceed this estimated exposure-time, as the exposure-time calculation does not include pre-calibrations and stage movement during exposure.

The area of your pattern can easily be found in L-edit by selecting all of your structure and use the area calculator in Tools/Add-Ins. If your pattern contains instances, you have to flatten your pattern (Cell/Flatten) before you use the area calculator; notice, however, that the flattening cannot be undone.

Beam diameter versus Beam current: The machine have three operating objective apertures (no. 15 on above illustration of the column) in order to obtain different beam diameters in different current ranges. The available apertures are called 'aperture 5' (60 µm), 'aperture 6' (100 µm) and 'aperture 7' (200 µm).