Specific Process Knowledge/Etch/KOH Etch/ProcessInfo

Feedback to this page: click here

Unless anything else is stated, everything on this page, text and pictures are made by DTU Nanolab.

QC

Quality Control (QC) for the KOH Si etching baths.

All links in the table below reguire login to labmanager**

Quality Control (QC) for Si Etch 01, and Si Etch 02

The QC procedure for Si Etch: 01 and Si Etch 02: KOH The QC procedure for Si Etch: 03 QC Recipe:   Solution 28 wt% KOH Temperature 80°C Time 90 min Elevator On Substrate Si (100) Masking Thermal SiO2 QC limits Si Etch 1 Si Etch 2 Si Etch 3 Etch rate in Si(100) Latest QC Data on Si Etch 1 Info page (under Documents) Latest QC Data on Si Etch 2 Info page (under Documents) Latest QC Data on Si Etch 3 Info page (under Documents) Roughness Only evaluated visually Only evaluated visually Only evaluated visually Nonuniformity < 3% < 3% < 3%

Mixing KOH

Nanolabs standard solution in the KOH baths has a concentration of 28 wt% and is mixed of 1 liter of a premade 50wt% KOH solution to 1.2 l of water.

If you use the 50wt% premade KOH solution you can calculate the amount of solution X you need to add 1 liter of water to achieve a concentration of Y wt% by:

${\frac {(0.5\cdot 1.509g/ml\cdot X)}{(X\cdot 1.509g/ml+1000g)}}=Y$

$X={\frac {(Y\cdot 1000g)}{(1.509g/ml\cdot (0.5-Y))}}$

where 1.509 g/ml is the density of a 50wt% solution KOH at 20 °C.

So for a 10 wt% solution you will need 165 ml of KOH (50wt%) to 1 l of water.

Backside protection

It is possible to protect the backside of the wafer against the KOH etch using special wafer holder.

Nanolab has backside protection holders for the two baths KOH 2 and KOH 3 for 4” wafer, and it is possible to mount two wafers in one holder. The material is PEEK, which is suitable for nearly all etchants and you will find the holders by the KOH baths. The recommended space from the wafer edge to your pattern is 7 mm. The thickness of the wafer would typically be 350 μm and the wafer would typically be polished on both sides, however with the right gasket (contact wet chemistry) the holders can accommodate 500-525 μm wafers. In order to avoid differences in pressure between the backside of the wafer and the surrounding environment, the venting tubes should be filled with water. The holder is clamped around the wafers by screws, if these screws are tightened too much or too little, it will affect the etching result. For the KOH 2 bath we have another type of holder which is clamped around the wafer with clamps (it cannot be adjusted to another wafer thickness). See more specific details about the screwed holders here, the holders we have at Nanolab is the Tandem4 type.

Theory

Definition of structures

Due to the almost inert (111)-planes it is possible by KOH etching to realize high aspect ratio structures in sigle crytalline silicon using the (111)-planes as sidewalls. In Si(100) these sidewalls are inclined - 54.7^o with respect to the (100) surface - whereas in Si(110) the sidewalls are vertical (see figures below).

• Anisotropic wet silicon etch: dependency on crystal orientation
• 
  Etched profile when etching Si(100) and when etching Si(110) respectively

For Si(100), the relation between the width of the bottom of the etched groove (W_b) and the width of the opening (W_o) at the wafer surface in a groove etched to the depth d is given by:

$W_{b}=W_{o}-2dcot(54.7^{o})=W_{o}-{\sqrt {2}}d$

Definition of <110> alignment structures

The etch rate dependence on the crystallographic planes can be used to determine the <110> crystal directions with high precision (better than +/- 0.05 ^o). A fast method for doing this, using the symmetric under-cutting behavior around but not at the <110>-directions, was described by Mattias Vangbo and Ylva Bäcklund 1996 J. Micromech. Microeng. 6, 279-284. High-precision control of the <110>-direction during alignment can be necessary in order to control the dimensions of KOH-etched structures (e.g. precise control of V-groove dimensions).