The Philips DCD IIH x-ray diffractometer used to characterize the layers on epitaxial semiconductor structures - usually III-V compound semiconductors.

The X-Ray Diffractometer is maintained by DTU fotonik (not Nanolab) and is therefore not in LabManager!

Nanolab also has a X-Ray Diffractometer for public acess. You can see it by clicking HERE

X-ray diffraction is a non-destructive technique to measure the lattice mismatch of epitaxial grown layers. The resulting measurements are also know as rocking-curves. In this way it is possible to get the relative content of e.g. In in Ga_xIn_1-xAs grown on InP. Ga_0.47In_0.53As is lattice-matched to InP. Compunds containing three different materials are also called ternaries. For more complex compounds containing 4 elements, known as quaternaries, e.g. Ga_xIn_1-xAs_yP_1-y, it is possible to obtain both x and y by combining x-ray diffraction measurements and PL-measurements (see PL Mapper).

Equipment performance and process related parameters

Performance	Excitation	x-ray tube Cu K-alpha (KFailed to parse (SVG (MathML can be enabled via browser plugin): Invalid response ("Math extension cannot connect to Restbase.") from server "https://wikimedia.org/api/rest_v1/":): {\displaystyle \alpha} ) 1.5418 Å
	Detection	counter
	Sample size	from 5x5mm up to 4" approximately
	Resolution	?? arc-sec
Materials	Allowed substrate materials	III-V Silicon