Specific Process Knowledge/Thermal Process/Annealing

Feedback to this page: click here

Annealing

At DTU Nanolab we have five furnaces and an RTP (Rapid thermal annealing) that can be used annealing: Anneal-Oxide furnace (C1), Anneal-bond furnace (C3), Al_anneal furnace (C4), Multipurpose Anneal furnace, Noble furnace and Jipelec RTP. Annealing normally takes place in an N₂ atmosphere, or it can be done in H₂ or a H₂-N₂ gas mixture in the Multipurpose Anneal furnace. PECVD PBSG glass is annealed in a wet atmosphere which will also oxidize the silicon substrate.

A 20 minutes N₂ annealing step is also included in all recipes on the oxidation furnace, this annealing is done after the oxidation.

Comparison of the annealing furnaces

	Anneal Oxide furnace (C1)	Anneal-Bond furnace (C3)	Aluminium Anneal furnace (C4)	Noble furnace	Jipelec RTP	Multipurpose Anneal Furnace
General description	Annealing of 4" and 6" wafers. Annealing of wafers from the LPCVD furnaces and from PECVD4.	Annealing of wafers from Wafer Bonder 02 and from and PECVD4 and PECVD3.	Annealing of wafers with Al and ALD deposited AL2O3 and TiO2.	Annealing of almost all materials on silicon wafers.	Rapid thermal annealing	Annealing, oxidation and resist pyrolysis of different samples
Annealing gas	N2	N2	N2	N2	N2 Vacuum is possible	N2 H2 H2-N2 gas mixture Vacuum is possible
Process temperature	700 oC - 1100 oC	700 oC - 1150 oC	Up to 500 oC	20 oC - 1000 oC	20 oC - 1000 oC Ramp up to 300 C/min	Vacuum: 20 oC - 1050 oC¨ No vacuum: 20 oC - 1100 oC
Substrate and Batch size	Small samples on a carrier wafer, horizontal 1-30 50 mm wafers 1-30 100 mm wafers 1-30 150 mm wafers	Small samples on a carrier wafer, horizontal 1-30 50 mm wafers 1-30 100 mm wafers	1-30 50 mm wafers 1-30 100 mm wafers	Small samples on a carrier wafer, horizontal 1-25 50 mm wafers 1-25 100 mm wafers, vertical and horizontal	Small samples on a carrier wafer, horizontal One 100 mm wafers on a carrier wafer	1-30 50 mm, 100 mm or 150 mm wafers 1-50 200 mm wafers Small samples on a carrier wafer, horizontal
Allowed materials	All processed wafers have to be RCA cleaned, except wafers from LPCVD furnaces and PECVD4.	All processed wafers have to be RCA cleaned, except wafers from the Wafer Bonder 02 and from PECVD4 and PECVD3.	Wafers with Al	Almost all materials, permission is needed.	III-V samples Silicon wafers Some metals	Depends on the furnace quartz ware: Clean: Samples that have been RCA cleaned Metal: Almost all materials, permission is needed Resist pyrolysis