Specific Process Knowledge/Thin film deposition/Deposition of Chromium: Difference between revisions
No edit summary |
No edit summary |
||
| Line 48: | Line 48: | ||
== Studies of Cr deposition processes == | == Studies of Cr deposition processes == | ||
[[/Deposition of Chromium|Uniformity of Cr layers]] - | [[/Deposition of Chromium|Uniformity of Cr layers]] - ''Uniformity of Cr layers deposited with different settings'' | ||
[[/Deposition of Chromium|Sputtering Cr Wordentec]] - | [[/Deposition of Chromium|Sputtering of Cr in Wordentec]] - ''Sputtering of Cr in Wordentec (settings and rates)'' | ||
Revision as of 13:37, 8 August 2008
Chromium can be deposited by e-beam evaporation. It should be noted that Chromium does not melt but evaporates directly from the solid phase. In the chart below you can compare the different deposition equipment.
| E-beam evaporation (Alcatel) | E-beam evaporation (Leybold) | E-beam evaporation (Wordentec) | Sputter deposition (Wordentec) | |
|---|---|---|---|---|
| Batch size |
|
|
|
|
| Pre-clean | RF Ar clean | Ar ion bombartment | RF Ar clean | RF Ar clean |
| Layer thickness | 10Å to 1µm | 10Å to 0.5µm | 10Å to 1µm | . |
| Deposition rate | 2Å/s to 15Å/s | 1Å/s to 5Å/s | 10Å/s to 15Å/s | . |
Studies of Cr deposition processes
Uniformity of Cr layers - Uniformity of Cr layers deposited with different settings
Sputtering of Cr in Wordentec - Sputtering of Cr in Wordentec (settings and rates)