Specific Process Knowledge/Etch/Wet Silicon Oxide Etch (BHF)

Wet Silicon Oxide Etch (BHF and SIO Etch (wetting agent))

Wet Silicon Oxide Etch (BHF): positioned in cleanroom 3

Silicon oxide can be etched using HF. At Danchip it is mainly used in a buffered version BHF (premixed). The BHF has a more stable etch rate and more gentle to photoresist due to an almost pH neutral solution which makes photoresist a good masking material for the oxide etch.

SIO etch (BHF with wetting agent) can also be used for etching silicon oxide. This is mainly for etching small holes. If you have wetting problems in BHF try the SIO etch. It is also a good idea to wet the sample in water before etching.

Silicon oxide etch data

	BHF	5% HF	SIO
General description	Etching of silicon oxide with a stable etch rate	Mainly for removing native oxide	Etching of silicon oxide - especially for etching small holes
Chemical solution	BHF	5% HF	BHF with wetting agent
Process temperature	Room temperature	Room temperature	Room temperature
Possible masking materials	Photoresist Silicon nitride PolySi Blue film	In beaker or PP-bath in the fume hood in cleanroom 2: Photoresist Silicon nitride PolySi Blue film In RCA bench: No masking material	Photoresist Silicon nitride PolySi Blue film
Etch rate	Wet thermal oxide:~80nm/min PECVD1 (standard):~147nm/min TEOS:~265nm/min	Wet thermal oxide:~25nm/min PECVD1 (standard):~87nm/min TEOS:~153nm/min	Wet thermal oxide:~80nm/min PECVD1 (standard):~147nm/min TEOS:~265nm/min
Life time of the photoresist	~½ hour	~½ hour	~½ hour
Batch size	1-25 wafers of 4" at a time	Beaker: 1-5 wafer of 4" at a time RCA bench: 1-25 wafers of 4" at a time	1-25 wafer of 4" at a time
Size of substrate	4" wafers	2"-6" wafers	4" wafers
Allowed materials	Silicon Silicon nitrides Silicon oxides Photoresist	In beaker or PP-bath in the fume hood in cleanroom 2: All materials In RCA bench: Only new wafers from the box or during RCA cleaning	Silicon Silicon nitrides Silicon oxides Photoresist

SIO etch (BHF with wetting agent): positioned in cleanroom 4

Life time of the photoresist and blue film in BHF

Photoresist delaminates from the substrate in BHF. For standard photoresist this process starts after about or less than ½ hour but the time can vary with resist pattern. It starts by under etching the photoresist at the edges. The life time can be prolonged a little to ½ hour - 40 minutes if the photoresist is baked at 120^oC.

Blue film also has a limited life time in BHF. Blue film is mainly used for back side protecting the wafer while etching on the front side. The life time of Blue film is also about ½ hour.