Specific Process Knowledge/Etch/Wet Silicon Nitride Etch

Wet Silicon Nitride Etch

Wet nitride etch: positioned in cleanroom 4

Wet Etching of silicon nitride is done in a dedicated laminar flow bench with an integrated quartz tank (Tiger Tank - TT-4). The quartz tank can take up to one 6" wafer carrier. The flow bench is placed in cleanroom 4. The process is mainly used to strip silicon nitride (maskless), but can also be used for masked etching of silicon nitride using some kind of silicon oxide as etch mask. However, the wet silicon nitride etch is isotropic meaning that the under-etching (etch-bias) at least amounts to the thickness of the silicon nitride layer.

The etch solution is initially 85 wt% H$3$PO$4$ which is heated up to the boiling temperature - ca. 157 ^oC. Water is allowed to boil off thus raising the concentration and the boiling temperature of the solution until a boiling temperature of 180 ^oC is reached. Thereafter, the wafers are submerged into the bath and the water-cooled lid is closed to maintain the concentration and the boiling temperature. In some cases a lower boiling temperature is chosen - typically 160 ^oC - which lowers the etch rate and improves the selectivity R_Si3N4 / R_SiO2

Nitride etch - key facts

	Nitride etch @ 180 oC	Nitride etch @ 160 oC
General description	Etch of silicon nitride	Etch of pure Gold
Chemical solution	KJ:J$_{2}$:H$_{2}$O (100g:25g:500ml)	HCl:HNO$_{3}$ (3:1)
Process temperature	20 oC	20 oC
Possible masking materials:	Photoresist (1.5 µm AZ5214E)	Photoresist (1.5 µm AZ5214E)
Etch rate	~100 nm/min (Pure Al)	~(??) nm/min
Batch size	1-25 wafers at a time	1-25 wafer at a time
Size of substrate	2-6" wafers	2-6" wafers