Specific Process Knowledge/Lithography/CSAR: Difference between revisions
No edit summary |
No edit summary |
||
| Line 108: | Line 108: | ||
|2000 | |2000 | ||
|4000 | |4000 | ||
| | |225.98 | ||
| | |0.97 | ||
|- | |- | ||
| Line 116: | Line 116: | ||
|3000 | |3000 | ||
|4000 | |4000 | ||
| | |194.00 | ||
| | |0.6 | ||
|- | |- | ||
| Line 124: | Line 124: | ||
|4000 | |4000 | ||
|4000 | |4000 | ||
| | |169.57 | ||
| | |0.32 | ||
|- | |- | ||
| Line 132: | Line 132: | ||
|5000 | |5000 | ||
|4000 | |4000 | ||
| | |151.47 | ||
| | |0.26 | ||
|- | |- | ||
| Line 140: | Line 140: | ||
|6000 | |6000 | ||
|4000 | |4000 | ||
| | |142.38 | ||
| | |0.41 | ||
|- | |- | ||
| Line 148: | Line 148: | ||
|7000 | |7000 | ||
|4000 | |4000 | ||
| | |126.59 | ||
| | |0.36 | ||
|- | |- | ||
|} | |} | ||
Revision as of 15:01, 10 April 2014
These tests are currently in progress and this page thus under construction. If you have questions to the process or wish to use this e-beam resist, please contact Tine Greibe at tigre@danchip.dtu.dk.
Test of Chemically Semi-Amplified Resist (CSAR); a positive e-beam resist from AllResist (AR-P 6200-2).
| Equipment | Process Parameters | Comments | Initials and date |
|---|---|---|---|
| Spin Coat of AllResist AR-P 6200-2 | |||
| Spin Coater Manual, LabSpin, A-5 | 60 sec at various spin speed. Acceleration 4000 s-2, softbake 5 min at 150 deg Celcius | Resist poured directly from bottle | TIGRE, 09-04-2014 |
| Characterization | |||
| Ellipsometer VASE B-1 | 9 points measured on 100 mm wafer | ZEP program used; measured at 70 deg only | TIGRE, 09-04-2014 |
| E-beam Exposure | |||
| JEOL 9500 E-beam writer, E-1 | Dosepattern 14nm - 100nm, dose 120-280 muC/cm2 | Virtual chip mark height detection | TIGRE, 10-04-2014 |
| Development | |||
| Fumehood, D-3 | 60 sec in X AR 600-54/6, 60 sec rinse in IPA, N2 Blow dry | Agitation (by hand) while developing | TIGRE, 10-04-2014 |
| Characterization | |||
| Zeiss SEM Supra 60VP, D-3 | TIGRE, ??-04-2014 | ||
| AllResist SX 6200/2 spinning on Manual Spinner LabSpin A-5, TIGRE, 09-04-2014 | ||||||
|---|---|---|---|---|---|---|
| Spin Speed [rpm] | Acceleration [1/s2] | Thickness [nm] | St Dev | |||
| 2000 | 4000 | 225.98 | 0.97 | |||
| 3000 | 4000 | 194.00 | 0.6 | |||
| 4000 | 4000 | 169.57 | 0.32 | |||
| 5000 | 4000 | 151.47 | 0.26 | |||
| 6000 | 4000 | 142.38 | 0.41 | |||
| 7000 | 4000 | 126.59 | 0.36 | |||