Specific Process Knowledge/Lithography/CSAR: Difference between revisions
No edit summary |
No edit summary |
||
| Line 1: | Line 1: | ||
These tests are currently in progress and this page thus under construction. If you have questions to the process or wish to use this e-beam resist, please contact Tine Greibe at tigre@danchip.dtu.dk. | |||
Test of Chemically Semi-Amplified Resist (CSAR); a positive e-beam resist from AllResist (AR-P 6200-2). | Test of Chemically Semi-Amplified Resist (CSAR); a positive e-beam resist from AllResist (AR-P 6200-2). | ||
| Line 9: | Line 13: | ||
!Process Parameters | !Process Parameters | ||
!Comments | !Comments | ||
!Initials and date | |||
|- | |- | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
!colspan=" | !colspan="4"|Spin Coat of AllResist AR-P 6200-2 | ||
|- | |- | ||
| Line 22: | Line 27: | ||
|60 sec at various spin speed. Acceleration 4000 s-2, softbake 5 min at 150 deg Celcius | |60 sec at various spin speed. Acceleration 4000 s-2, softbake 5 min at 150 deg Celcius | ||
|Resist poured directly from bottle | |Resist poured directly from bottle | ||
|TIGRE, 09-04-2014 | |||
|- | |- | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
!colspan=" | !colspan="4"|Characterization | ||
|- | |- | ||
| Line 32: | Line 38: | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
|Ellipsometer VASE B-1 | |Ellipsometer VASE B-1 | ||
|9 points measured on 100 mm wafer | |||
|ZEP program used; measured at 70 deg only | |ZEP program used; measured at 70 deg only | ||
| | |TIGRE, 09-04-2014 | ||
|- | |- | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
!colspan=" | !colspan="4"|E-beam Exposure, | ||
|- | |- | ||
| Line 47: | Line 54: | ||
|Dosepattern 14nm - 100nm, dose 120-280 muC/cm2 | |Dosepattern 14nm - 100nm, dose 120-280 muC/cm2 | ||
|Virtual chip mark height detection | |Virtual chip mark height detection | ||
| TIGRE, 10-04-2014 | |||
|- | |- | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
!colspan=" | !colspan="4"|Development, | ||
|- | |- | ||
| Line 59: | Line 67: | ||
|60 sec in X AR 600-54/6, 60 sec rinse in IPA, N2 Blow dry | |60 sec in X AR 600-54/6, 60 sec rinse in IPA, N2 Blow dry | ||
|Agitation (by hand) while developing | |Agitation (by hand) while developing | ||
| TIGRE, 10-04-2014 | |||
|- | |- | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |-style="background:WhiteSmoke; color:black" | ||
!colspan=" | !colspan="4"|Characterization, | ||
|- | |- | ||
| Line 71: | Line 80: | ||
| | | | ||
| | | | ||
| TIGRE, ??-04-2014 | |||
|- | |- | ||