Comparing the three bonding methods in the EVG NIL
Choose equipment
Choose bonding methods in EVG NIL
| Eutectic bonding | Fusion bonding | Anodic bonding | |
| General description |
For bonding two substrates by use of an interphase that makes an eutecticum. |
For bonding two identical materials. |
For bonding Si and Glass. |
| Bonding temperature |
Depending on the eutecticum 310°C to 400°C. |
Depending on defects 50°C to 400°C. |
Depending on the voltage 300°C to 500°C Standard is 400°C. |
| Annealing temperature |
No annealing |
1000°C in the bond furnace C3. |
No annealing |
| Materials possible to bond |
Bonding of substrates is done by use of the eutectica Au/Si, Au/Sn and Au/Sn/Ni |
Si/Si, SiO2/SiO2 |
Si/Pyrex (glass) |
| Substrate size |
Up to 6" (aligning only possible for 4" and 6") |
Up to 6" (aligning only possible for 4" and 6") |
Up to 6" (aligning only possible for 4" and 6") |
| Cleaning |
Cleaning by N2. |
Wet chemical cleaning, IMEC. |
Cleaning by N2. |
| IR alignment |
Double side polished wafers. |
Double side polished wafers. |
Not relevant. |