Jump to content

Specific Process Knowledge/Etch/DRIE-Pegasus/Pegasus-2/ORE with Al2O3 mask: Difference between revisions

← Older edit
VisualWikitext
Mfarin (talk | contribs)
NLAB-Employees-701, NLAB-LabmanagerAllUsers, NLAB-Nlab347-labadviser-users-35231
781 edits
Mfarin (talk | contribs)
NLAB-Employees-701, NLAB-LabmanagerAllUsers, NLAB-Nlab347-labadviser-users-35231
781 edits
No edit summary
 
(46 intermediate revisions by the same user not shown)
Line 2: Line 2:




=<span style="background:#FF2800">THIS PAGE IS UNDER CONSTRUCTION</span>[[image:Under_construction.png|200px]]=
''By Maria Farinha @Nanolab Internal, Jan 2023 if nothing more is stated''
''By Maria Farinha @Nanolab Internal, Jan 2023''


=Al<sub>2</sub>O<sub>3</sub> mask=
=Al<sub>2</sub>O<sub>3</sub> mask=


[[File:esq met Al2O3 compact.jpg|300px|right|thumb|'''''Scheme of the sample fabrication using Al<sub>2</sub>O<sub>3</sub> mask. These samples were coated with either 50 or 100 nm of Al<sub>2</sub>O<sub>3</sub>, followed by 65 nm of BARC and 750 nm of DUV resist. Not at scale. <br>
[[File:esq met Al2O3 compact.jpg|400px|right|thumb|'''''Scheme of the sample fabrication using Al<sub>2</sub>O<sub>3</sub> mask. These samples were coated with either 50 or 100 nm of Al<sub>2</sub>O<sub>3</sub>, followed by 65 nm of BARC and 750 nm of DUV resist. Not at scale. <br>
Scheme: Maria Farinha, @DTU Nanolab''''']]
Scheme: Maria Farinha, @DTU Nanolab''''']]


In these samples, the hard mask, Al<sub>2</sub>O<sub>3</sub>, was coated in 150 mm Si wafers using the ALD 1 tool. These sets of samples also had the lithography process done in the DUV stepper to deposit 65 nm of BARC and 750 nm of DUV resist. Three different patterns were created after the development:
In these samples, the hard mask, Al<sub>2</sub>O<sub>3</sub>, was coated in 150 mm Si wafers using the ALD 1 tool. These sets of samples also had the lithography process done in the DUV stepper to deposit 65 nm of BARC and 750 nm of DUV resist. Three different patterns were created after the development:


# Pillars of 1 µm with 1 µm pitch (50 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV).
# 1 µm width pillars with 1 µm pitch (50 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV resist).
# Holes of 1 µm with 1 µm pitch (50 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV).
# 1 µm width holes with 1 µm pitch (50 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV resist).
# Nanoholes of 200 nm with 400 nm pitch (100 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV).
# 200 nm width nanoholes with 400 nm pitch (100 nm Al<sub>2</sub>O<sub>3</sub> + 65 nm BARC + 750 nm DUV resist).
 
The Si / Al<sub>2</sub>O<sub>3</sub> / BARC / DUV stack was first processed in Pegasus 2 to etch the BARC layer (recipe named ''"barc gentle etch"'', ER=5.42nm/min), and the alumina was etched in the III-V ICP, using a BCl<sub>3</sub> / Ar recipe, which has an ER = 0.45 nm/min. With the pillars and holes samples, the BARC was also etched for 12 min on Pegasus 2, followed by 90 minutes on the III-V ICP. <br>
For the nanoholes, the Al<sub>2</sub>O<sub>3</sub> layer was etched for 260 minutes on the III-V ICP. The next thing would be to etch the BARC layer on Pegasus 2, however, it was seen that after the III-V ICP process, the leftover resist on the sample was removed during the CORE process on Pegasus 2, having no need to do the dedicated ''"barc gentle etch"'' recipe.
<br>
 
{| border="1" style="text-align: center; width: 800px; height: 200px"
|+ '''Samples profile before going for the ORE process:'''
|-
|-style="background:LightGray; color:Black"
! !! After Al<sub>2</sub>O<sub>3</sub> etch !! Comments
|-
| ''' 1 µm pillars''' || [[File:Pillar 0C+S-RIE Al2O3 02bbbb.jpg|300px]]  [[File:Pillar 0C+S-RIE Al2O3 08bbbb.jpg|300px]] || Visible that after the 90 min Al<sub>2</sub>O<sub>3</sub> etch, the mask was correctly etched away confirmed by reaching the silicon (etched ~30nm of it).
|-
| ''' 1 µm holes''' || [[File:bitmapddddd.jpg|300px]]  [[File:holes.tif.jpg|300px]] || Visible that after the 90 min Al<sub>2</sub>O<sub>3</sub> etch, the mask was correctly etched away confirmed by reaching the silicon (etched ~16nm of it).
|-
| '''200nm nanoholes''' || [[File:nanoHoles 0g 02 v3.jpg|300px]]  [[File:nanoHoles 0g 05 v2.jpg|300px]] || Visible that after the 260 min Al<sub>2</sub>O<sub>3</sub> etch, the mask was correctly etched away confirmed by reaching the silicon (etched ~20nm of it). Resist visible on top of the mask since it was etched during the ORE process.
|}
 
 
 


The Si / Al<sub>2</sub>O<sub>3</sub> / BARC / DUV stack was first processed in Pegasus 2 to etch the BARC layer, and the alumina was etched in the III-V ICP, using a BCl<sub>3</sub> / Ar recipe. With pillars and holes, the BARC was etched for 12 min on Pegasus 2, followed by 90 minutes on the III-V ICP. The nanoholes had two different approaches, starting with 260 minutes on the III-V ICP. However, it was seen that after the III-V ICP process, the leftover resist on the sample was removed during the CORE process on Pegasus 2.
<br clear="all" />
<br clear="all" />
After the Al<sub>2</sub>O<sub>3</sub> etch, pillars were:


=ORE process=
=ORE process=
Line 35: Line 52:


Using patterned samples of 1 μm pillars with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 32nm of Al<sub>2</sub>O<sub>3</sub> were still intact. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC, no coil power and all heaters OFF.
Using patterned samples of 1 μm pillars with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 32nm of Al<sub>2</sub>O<sub>3</sub> were still intact. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC, no coil power and all heaters OFF.
<br clear="all" />
<br clear="all" />
<br clear="all" />
[[File:compare pillars.png|400px|left|thumb|'''''Pillars with different etching times. <br>
[[File:compare pillars.png|400px|left|thumb|'''''Pillars with different etching times. <br>
Line 57: Line 75:
=== Holes ===
=== Holes ===
Using patterned samples of 1 μm holes with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 28nm of Al<sub>2</sub>O<sub>3</sub> were still intact. When using this recipe, by adjusting the number of cycles, approximately 10 μm was achieved maintaining a straight profile. When going for deeper profiles, 17 μm was also achieved, but the profile started to get positive. Further work may solve the issue. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF.
Using patterned samples of 1 μm holes with 50 nm of Al<sub>2</sub>O<sub>3</sub>. After the tests, approximately 28nm of Al<sub>2</sub>O<sub>3</sub> were still intact. When using this recipe, by adjusting the number of cycles, approximately 10 μm was achieved maintaining a straight profile. When going for deeper profiles, 17 μm was also achieved, but the profile started to get positive. Further work may solve the issue. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF.
<br clear="all" />
<br clear="all" />
[[File:holes 17 e 10 um.png|400px|left|thumb|'''''Holes profile. #144 cycles for 60 min and #288 cycles for 120 min.<br>
[[File:holes 17 e 10 um.png|400px|left|thumb|'''''Holes profile. #144 cycles for 60 min and #288 cycles for 120 min.<br>
Photo: Maria Farinha @DTU Nanolab, March 2022''''']]
Photo: Maria Farinha @DTU Nanolab, March 2022''''']]
Line 77: Line 97:


=== Nanoholes ===
=== Nanoholes ===
The nanoholes are 200nm wide, with 400nm pitch with 100 nm Al<sub>2</sub>O<sub>3</sub> mask. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF.
The nanoholes are 200nm wide, with 400nm pitch with 100 nm Al<sub>2</sub>O<sub>3</sub> mask. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF. The removal power was varied, and the achieved ER for 40W was 48.5 nm/min.
[[File:nH R-power.png|500px|left|thumb|'''''Nanoholes profile when varying the removal power.<br>
<br clear="all" />
<br clear="all" />
[[File:nH R-power.png|500px|left|thumb|'''''Nanoholes profile when varying the removal power. <br>
Photo: Maria Farinha @DTU Nanolab, April 2022''''']]
Photo: Maria Farinha @DTU Nanolab, April 2022''''']]
{| border="1" style="text-align: center; width: 650px; height: 200px"
{| border="1" style="text-align: center; width: 650px; height: 200px"
Line 97: Line 119:
<br clear="all" />
<br clear="all" />
The most suitable removal power was 40 W, removing the bottom of the profile correctly without damaging the top part of the profile.
The most suitable removal power was 40 W, removing the bottom of the profile correctly without damaging the top part of the profile.
 
<br clear="all" />
<br clear="all" />
[[File:nH E-time.png|500px|left|thumb|'''''Nanoholes profile when varying the ramping E-time .<br>
[[File:nH E-time.png|500px|left|thumb|'''''Nanoholes profile when varying the ramping E-time .<br>
Photo: Maria Farinha @DTU Nanolab, July 2022''''']]
Photo: Maria Farinha @DTU Nanolab, July 2022''''']]
Line 110: Line 133:
| '''R-step''' || 10 || 100% || 0 || 40 || 40
| '''R-step''' || 10 || 100% || 0 || 40 || 40
|-
|-
| '''E<sub>1</sub>-step''' || 2 || 220 mTorr || 0 || 350 || 40
| '''E<sub>1</sub>-step''' || 2 || 220 mTorr || 0 || 350 || 0
|-
|-
| '''E<sub>2</sub>-step''' || * || 220 mTorr || 0 || 350 || 300
| '''E<sub>2</sub>-step''' || * || 220 mTorr || 0 || 350 || 100-300
|} ''*The E<sub>2</sub>-time value was changed and observed.''
|} ''*The E<sub>2</sub>-time value was changed and observed.''
<br clear="all" />
<br clear="all" />
Regarding the measurements of the profiles, in a) the depth reached 3.17 µm with 0-15s of ramping, b) reached 3.21 µm with 1-15s of ramping, c) reached 2.87 µm whit 5-15s of ramping and d) reached 3.63 µm with 15 s without ramping.
Regarding the measurements of the profiles, in a) the depth reached 3.17 µm with 0-15s of ramping, b) reached 3.21 µm with 1-15s of ramping, c) reached 2.87 µm whit 5-15s of ramping and d) reached 3.63 µm with 15 s without ramping. Even though the etching ramping times may appear similar, there are differences in the feature profile. The ER for 0-15s and 1-15s is around 52 nm/min and for 5-15s and 15s is approximately 48 nm/min.


<br clear="all" />
<br clear="all" />
Line 121: Line 144:
=== Isotropic etch ===
=== Isotropic etch ===


Some isotropic etches were performed, intercalated with anisotropic etches. The nanoholes are 200nm wide, with 400nm pitch with 100 nm Al<sub>2</sub>O<sub>3</sub> mask. The recipe presented in the table was repeated either 2 or 3 times in order to achieve the picture results. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF.
Some isotropic etches were performed, intercalated with anisotropic etches. The nanoholes are 200nm wide, with 400nm pitch with 100 nm Al<sub>2</sub>O<sub>3</sub> mask. The recipe presented in the table was repeated 2 or 3 times to achieve the picture results. During the recipe, Pegasus 2 conditions were: Outer EM=10A, T=20°C, no clamping, no He BGC and all heaters OFF. Trying to oxide the sample before doing the isotropic etch can help to protect the top part, maintaining a more straight profile. However, after trying to do an oxidation step on Pegasus 2, with 3% valve control. 200 sccm O<sub>2</sub> and 2000W of coil power, the oxide layer was only 3.2 nm.
<br clear="all" />
<br clear="all" />
[[File:cpr + iso x2 meas.png|400px|left|thumb|'''''x2 anisotropic + isotropic etch.<br>
[[File:cpr + iso x2 meas.png|400px|left|thumb|'''''x2 anisotropic + isotropic etch.<br>
Photo: Maria Farinha @DTU Nanolab, June 2022''''']]
Photo: Maria Farinha @DTU Nanolab, June 2022''''']]
Line 202: Line 227:




<!--
<br clear="all" />
-->
 
==Previous work on Peg2==
 
*[https://run.unl.pt/bitstream/10362/152030/1/Farinha_2022.pdf SF6/O2 Plasma Etching: Optimizing the CORE process and going into 3D Engineering_November22 by Maria Farinha@DTU Nanolab]