Specific Process Knowledge/Thin film deposition/Deposition of Titanium Nitride: Difference between revisions

From LabAdviser
Paphol (talk | contribs)
Reet (talk | contribs)
No edit summary
 
(One intermediate revision by one other user not shown)
Line 1: Line 1:
'''Feedback to this page''': '''[mailto:labadviser@nanolab.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.nanolab.dtu.dk/index.php/Specific_Process_Knowledge/Thin_film_deposition/Deposition_of_Titanium_Nitride click here]'''
'''Feedback to this page''': '''[mailto:labadviser@nanolab.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.nanolab.dtu.dk/index.php/Specific_Process_Knowledge/Thin_film_deposition/Deposition_of_Titanium_Nitride click here]'''


''All text by Nanolab staff''
<br clear="all" />
<br clear="all" />


Line 69: Line 70:
* 0.0232 nm/cycle on a high aspect ratio structures
* 0.0232 nm/cycle on a high aspect ratio structures
|
|
* about 7 nm/min, depends on sputtering parameters, check processlog in LabManager
* about 0.12 nm/s, depends on sputtering parameters, check processlog in LabManager
|
|
* up to 0.0625 nm/s on a flat sample
* up to 0.0625 nm/s on a flat sample

Latest revision as of 13:39, 2 June 2023

Feedback to this page: click here

All text by Nanolab staff

Deposition of Titanium Nitride

Thin films of Titanium Nitride (TiN) can be deposited by either ALD or reactive sputtering. If sputtering is used, the target is Ti and nitrogen (N2) is added as reactive gas to the chamber resulting the formation of Titanium Nitride on the sample. The process information is available below:

Comparison between sputtering and ALD methods for deposition of Titanium Nitride.

ALD2 Sputter-System Metal-Oxide (PC1)/Sputter-System Metal-Nitride (PC3) Sputter-System(Lesker)
Generel description
  • Atomic Layer Deposition
  • Reactive sputtering
  • Pulsed DC reactive sputtering
  • Reactive HIPIMS (high-power impulse magnetron sputtering)
  • Reactive sputtering
Stoichiometry
  • TiN
  • TiN (can be tuned)
  • TiN (can be tuned)
Film Thickness
  • 0 nm - 50 nm
  • few nm - ? (hundreds of nm)
  • few nm - 200 nm
Deposition rate
  • 0.0173 nm/cycle on a flat sample
  • 0.0232 nm/cycle on a high aspect ratio structures
  • about 0.12 nm/s, depends on sputtering parameters, check processlog in LabManager
  • up to 0.0625 nm/s on a flat sample
Step coverage
  • Very good
  • not known yet
  • Not investigated
Process Temperature
  • 450 °C
  • Up to 600 °C
  • Up to 400 °C
Substrate size
  • Several small samples
  • 1-5 50 mm wafers
  • 1-5 100 mm wafers
  • 1-5 150 mm wafer
  • Many small samples
  • Up to 10x100 mm or 150 mm wafers
  • Several small samples
  • 100 mm wafer
  • 150 mm wafer
Allowed materials
  • Silicon
  • Silicon oxide, silicon nitride
  • Quartz/fused silica
  • Al, Al2O3
  • Ti, TiO2
  • Other metals (use dedicated carrier wafer)
  • III-V materials (use dedicated carrier wafer)
  • Polymers (depending on the melting point/deposition temperature, use carrier wafer)
  • Silicon
  • Silicon oxide, silicon nitride
  • Quartz/fused silica
  • Metals
  • III-V materials (use dedicated carrier wafer)
  • Almost anything that is not toxic and does not outgas
  • Silicon
  • Silicon oxide, silicon nitride
  • Quartz/fused silica
  • Metals
  • III-V materials (use dedicated carrier wafer)
  • Almost anything that is not toxic