Specific Process Knowledge/Thermal Process/A3 Phosphor Drive-in furnace: Difference between revisions

From LabAdviser
← Older edit
VisualWikitext
Pevo (talk | contribs)
DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers
2,009 edits
No edit summary
Paphol (talk | contribs)
DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers
898 edits
 
(15 intermediate revisions by 3 users not shown)
Line 1: Line 1:
'''Feedback to this page''': '''[mailto:thinfilm@danchip.dtu.dk?Subject=Feed%20back%20from%20page%20http://http://labadviser.danchip.dtu.dk/index.php/Specific_Process_Knowledge/Thermal_Process/A3_Phosphor_Drive-in_furnace click here]'''
'''Feedback to this page''': '''[mailto:thinfilm@nanolab.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.danchip.dtu.dk/index.php/Specific_Process_Knowledge/A3_Phosphor_Drive-in_furnace click here]'''
 
''This page is written by DTU Nanolab  internal''


[[Category: Equipment |Thermal A3]]
[[Category: Equipment |Thermal A3]]
Line 5: Line 7:
[[Category: Furnaces|A3]]
[[Category: Furnaces|A3]]


==Phosphorus Drive-in furnace (A3)==
[[Image:A3helstak.jpg|thumb|400x400px|Phosphorus Drive-in furnace (A3). Positioned in cleanroom B-1/ Photo: DTU Nanolab internal]]
The Phosphorus Drive-in furnace (A3) is a Tempress horizontal furnace for thermal oxidation of silicon wafers. Furthermore, the furnace is used for phosphorus drive-in afte pre-deposition/doping or after boron ion implantation.


==Phosphorus Drive-in furnace (A3)==
The furnace is mostly used for wet and dry thermal oxidation of silicon wafers. The oxidation recipes are named e.g. "WET1000" and "DRY1000", where "WET" or "DRY" indicates whether it is a wet or dry oxidation process, and the number indicates the oxidation temperature.  
[[Image:A3helstak.jpg|thumb|300x300px|Phosphorus Drive-in furnace (A3). Positioned in cleanroom B-1]]


The Phosphorus Drive-in furnace (A3) is a Tempress horizontal furnace for oxidation of silicon wafers, annealing of the grown oxide layer and for drive-in of phosphorus after a pre-deposition. Phosphorus pre-deposition takes place in the Phosphorus Pre-dep furnace (A4). The Phosphorus Drive-in furnace can also be used for drive-in of phosphorus which has been ion implanted.  
The purpose of phosphorus doping is to make conductive structures, etch stop layers etc. After a phosphorus pre-deposition/doping or ion implantation process, a drive-in process with or without an oxide growth is done in the furnace. The phosphorus pre-deposition is normally done in the Phosphorus Pre-dep (A4) furnace, and ion implantation have to be done elsewhere.  


The Phosphorus Drive-in furnace is the third furnace tube in the A-stack positioned in cleanroom B-1. The furnaces in the A-stack are the cleanest of all furnaces in the cleanroom. Please be aware of that all wafers have to be RCA cleaned before they enter the furnace, and check the cross contamination information in LabManager before you use the furnace.
The Phosphorus Drive-in furnace is the third furnace tube in the A-stack positioned in cleanroom B-1. The furnaces in the A-stack are the cleanest of all furnaces in the cleanroom. Please be aware of that all wafers have to be RCA cleaned before they enter the furnace (except wafers coming form the Phosphorus Pre-dep furnace that have been BHF etched in the dedicated bath in the RCA bench), and please check the cross contamination information in LabManager, before you use the furnace.  




Line 17: Line 22:


'''[http://www.labmanager.danchip.dtu.dk/function.php?module=Machine&view=view&mach=82 Phosphorus Drive-in furnace (A3)]'''
'''[http://www.labmanager.danchip.dtu.dk/function.php?module=Machine&view=view&mach=82 Phosphorus Drive-in furnace (A3)]'''


==Process knowledge==
==Process knowledge==
*Phosphorus drive-in: look at the [[Specific Process Knowledge/Thermal Process/Dope with Phosphorus|Dope with Phosphorus]] page
*Oxidation: look at the [[Specific Process Knowledge/Thermal Process/Oxidation|Oxidation]] page
*Oxidation: look at the [[Specific Process Knowledge/Thermal Process/Oxidation|Oxidation]] page
*Annealing: look at the [[Specific Process Knowledge/Thermal Process/Annealing|Annealing]] page
*Phosphorus drive-in: look at the [[Specific Process Knowledge/Thermal Process/Dope with Phosphorus|Dope with Phosphorus]] page




Line 30: Line 33:
|-
|-
|
|
*[http://www.labmanager.danchip.dtu.dk/d4Show.php?id=2847&mach=82 The QC procedure for Phosphorus drive-in furnace (A3)]<br>
*[http://labmanager.dtu.dk/d4Show.php?id=2847&mach=82 The QC procedure for Phosphorus drive-in furnace (A3)]<br>
*[http://www.labmanager.danchip.dtu.dk/view_binary.php?fileId=1988 The newest QC data for wet and dry oxide]<br>
*[https://labmanager.dtu.dk/view_binary.php?type=data&mach=82 The newest QC data for wet and dry oxide]<br>


{| {{table}}
{| {{table}}
Line 38: Line 41:


! QC Recipe:
! QC Recipe:
! Wet1050
! WET1050
! Dry1050
! DRY1050
|-  
|-  
| H<sub>2</sub> flow
| H<sub>2</sub> flow
Line 50: Line 53:
|-  
|-  
|Temperature
|Temperature
|1050 C
|1050 <sup>o</sup>C
|1050 C
|1050 <sup>o</sup>C
|-
|-
|Oxidation time
|Oxidation time
Line 66: Line 69:
and over the boat)
and over the boat)
|-
|-
!Dry1050
!DRY1050
|110-116 nm
|110-116 nm
|3 %
|3 %
|-
|-
!Wet1050
!WET1050
|305-321 nm
|305-321 nm
|5 %
|5 %
Line 77: Line 80:
|-
|-
|}
|}
Numbers from March 2020
|}
|}


==Overview of the performance of the phosphorus drive-in furnace and some process related parameters==
==Overview of the performance of the phosphorus drive-in furnace and some process related parameters==
Line 86: Line 89:
!style="background:silver; color:black;" align="center"|Purpose  
!style="background:silver; color:black;" align="center"|Purpose  
|style="background:LightGrey; color:black"|
|style="background:LightGrey; color:black"|
*Drive-in of phosphorous
*Thermal oxidation of Si wafers
*Oxidation of silicon
*Driving-in pre-deposited or ion-implanted phosphorus
*Oxidation of phosphorous phase layers
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|Oxidation:
Thermal oxidation:
*Dry
*Dry oxidation using O<sub>2</sub>
*Wet: with torch (H<sub>2</sub>+O<sub>2</sub>)
*Wet oxidation using H<sub>2</sub>O vapour
Driving-in pre-deposited or ion-implanted phosphorus
*Dry or wet oxidation recipes are normally used for this purpose
|-
|-
!style="background:silver; color:black" align="center"|Performance
!style="background:silver; color:black" align="center"|Performance
|style="background:LightGrey; color:black"|Film thickness
|style="background:LightGrey; color:black"|Film thickness
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|
*Dry SiO<sub>2</sub>: 50 Å  to ~2000 Å (it takes too long to grow a thicker oxide layer)
*Dry oxide: ~ 0 nm - 300 nm (it takes too long to grow a thicker oxide)
*Wet SiO<sub>2</sub>: 50 Å to ~3 µm (it takes too long to grow a thicker oxide layer)
*Wet oxide: ~ 0 nm - 3 µm (23 hours wet oxidation at 1100 <sup>o</sup>C for Si[100] wafers)  
|-
|-
!style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range
!style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range
|style="background:LightGrey; color:black"|Process Temperature
|style="background:LightGrey; color:black"|Process Temperature
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|
*800-1150 <sup>o</sup>C
*800 <sup>o</sup>C - 1150 <sup>o</sup>C
|-
|-
|style="background:LightGrey; color:black"|Process pressure
|style="background:LightGrey; color:black"|Process pressure
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|
*1 atm
*1 atm (no vacuum)
|-
|-
|style="background:LightGrey; color:black"|Gasses on the system
|style="background:LightGrey; color:black"|Gasses on the system
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|
*O<sub>2</sub>, N<sub>2</sub> and H<sub>2</sub>
*N<sub>2</sub>
*O<sub>2</sub>
*H<sub>2</sub> (in a torch, H<sub>2</sub> and O<sub>2</sub> burns into H<sub>2</sub>O for wet oxidation)
|-
|-
!style="background:silver; color:black" align="center" valign="center" rowspan="2"|Substrates
!style="background:silver; color:black" align="center" valign="center" rowspan="2"|Substrates
Line 120: Line 127:
|style="background:WhiteSmoke; color:black"|
|style="background:WhiteSmoke; color:black"|
*Silicon wafers (RCA cleaned)
*Silicon wafers (RCA cleaned)
*Wafers from the the Phosphorus Pre-dep furnace can go directly into the furnace
*Wafers coming from the Phosphorus Pre-dep furnace that have been BHF etched in the dedicated bath in the RCA bench can go directly into the furnace
|-  
|-  
|}
|}

Latest revision as of 14:04, 31 January 2023

Feedback to this page: click here

This page is written by DTU Nanolab internal

Phosphorus Drive-in furnace (A3)

Phosphorus Drive-in furnace (A3). Positioned in cleanroom B-1/ Photo: DTU Nanolab internal

The Phosphorus Drive-in furnace (A3) is a Tempress horizontal furnace for thermal oxidation of silicon wafers. Furthermore, the furnace is used for phosphorus drive-in afte pre-deposition/doping or after boron ion implantation.

The furnace is mostly used for wet and dry thermal oxidation of silicon wafers. The oxidation recipes are named e.g. "WET1000" and "DRY1000", where "WET" or "DRY" indicates whether it is a wet or dry oxidation process, and the number indicates the oxidation temperature.

The purpose of phosphorus doping is to make conductive structures, etch stop layers etc. After a phosphorus pre-deposition/doping or ion implantation process, a drive-in process with or without an oxide growth is done in the furnace. The phosphorus pre-deposition is normally done in the Phosphorus Pre-dep (A4) furnace, and ion implantation have to be done elsewhere.

The Phosphorus Drive-in furnace is the third furnace tube in the A-stack positioned in cleanroom B-1. The furnaces in the A-stack are the cleanest of all furnaces in the cleanroom. Please be aware of that all wafers have to be RCA cleaned before they enter the furnace (except wafers coming form the Phosphorus Pre-dep furnace that have been BHF etched in the dedicated bath in the RCA bench), and please check the cross contamination information in LabManager, before you use the furnace.


The user manual, quality control instruction and results, technical information and contact information can be found in LabManager:

Phosphorus Drive-in furnace (A3)

Process knowledge


Quality Control - Recipe Parameters and Limits

Quality Control (QC) for the processes "Wet1050" and "Dry1050"
QC Recipe: WET1050 DRY1050
H2 flow 3 slm 0 slm
O2 flow 2 slm 5 slm
Temperature 1050 oC 1050 oC
Oxidation time 30 min 100 min
QC limits Thickness Non-uniformity (both over a single wafer

and over the boat)

DRY1050 110-116 nm 3 %
WET1050 305-321 nm 5 %

Numbers from March 2020

Overview of the performance of the phosphorus drive-in furnace and some process related parameters

Purpose
  • Thermal oxidation of Si wafers
  • Driving-in pre-deposited or ion-implanted phosphorus

Thermal oxidation:

  • Dry oxidation using O2
  • Wet oxidation using H2O vapour

Driving-in pre-deposited or ion-implanted phosphorus

  • Dry or wet oxidation recipes are normally used for this purpose
Performance Film thickness
  • Dry oxide: ~ 0 nm - 300 nm (it takes too long to grow a thicker oxide)
  • Wet oxide: ~ 0 nm - 3 µm (23 hours wet oxidation at 1100 oC for Si[100] wafers)
Process parameter range Process Temperature
  • 800 oC - 1150 oC
Process pressure
  • 1 atm (no vacuum)
Gasses on the system
  • N2
  • O2
  • H2 (in a torch, H2 and O2 burns into H2O for wet oxidation)
Substrates Batch size
  • 1-30 100 mm wafers (or 50 mm wafers) per run
Substrate materials allowed
  • Silicon wafers (RCA cleaned)
  • Wafers coming from the Phosphorus Pre-dep furnace that have been BHF etched in the dedicated bath in the RCA bench can go directly into the furnace