Specific Process Knowledge/Etch/III-V ICP/GaAs-AlGaAs: Difference between revisions
No edit summary |
No edit summary |
||
| (2 intermediate revisions by the same user not shown) | |||
| Line 2: | Line 2: | ||
===GaAs/AlGaAs etching using III-V ICP=== | ===GaAs/AlGaAs etching using III-V ICP=== | ||
'''''Recipes developed and/or tested by DTU Photonics internal before 2011''''' | |||
{| border="1" cellspacing="2" cellpadding="3" | {| border="1" cellspacing="2" cellpadding="3" | ||
| Line 135: | Line 135: | ||
{| border="1" cellspacing="2" cellpadding="3" | {| border="1" cellspacing="2" cellpadding="3" | ||
![[image:ICP_BCL3_result.jpg|300x300px|thumb|left|Result of GaAs etching with BCl<sub>3</sub>. Qijiang Ran, DTU Photonics, 2011. ]] | ![[image:ICP_BCL3_result.jpg|300x300px|thumb|left|Result of GaAs etching with BCl<sub>3</sub>. Done by: Qijiang Ran, DTU Photonics, 2011. ]] | ||
|- | |- | ||
|} | |} | ||
Latest revision as of 09:41, 10 February 2023
Feedback to this page: click here
GaAs/AlGaAs etching using III-V ICP
Recipes developed and/or tested by DTU Photonics internal before 2011
| Recipe | GaAs Etch |
| Cl2 flow | 4 sccm |
| Ar flow | 12 sccm |
| Platen power | 80 W |
| Coil power | 700 W |
| Pressure | 6 mTorr |
| Platen chiller temperature | 20 oC |
| Results (GaAs Etch) | |
| GaAs etch rate | >500 nm/min |
| Sidewall angle | ~ 85-90 o |
| Selectivity (GaAs:Si3N4, GaAs:AlInP) | 10:1, 5:1 |
| Recipe | GaAs_AlGaAs Etch |
| Cl2 flow | 20 sccm |
| N2 flow | 50 sccm |
| Platen power | 100 W |
| Coil power | 600 W |
| Pressure | 2 mTorr |
| Platen chiller temperature | 20 oC |
| Results (GaAs_AlGaAs Etch) | |
| AlGaAs etch rate | >1000 nm/min |
| Sidewall angle | ~ 90 o |
| Selectivity (GaAs:SiO2) | 30:1 |
| Recipe | GaAs_AlGaAs Etch_BCl3 |
| Cl2 flow | 10 sccm |
| BCl3 flow | 10 sccm |
| Ar flow | 10 sccm |
| N2 flow | 4 sccm |
| Platen power | 50 W |
| Coil power | 500 W |
| Pressure | 1 mTorr |
| Platen chiller temperature | 20 oC |
| Results (GaAs_AlGaAs Etch_BCl3) | |
| GaAs etch rate | >750 nm/min |
| Sidewall angle | 85-90 o |
| Selectivity (GaAs:Si3N4, GaAs:AlInP) | 10:1 |
 |
|---|