New page: ; Question 1 : I remember you said that you don't like Al as masking material because it will get sputtered off (am I right?) - but what about ALD deposited aluminium oxide - it is, as fa...
 
Jmli (talk | contribs)
DCH-Employees-701, NLAB-Employees-701, NLAB-LabmanagerAllUsers
4,416 edits
Blanked the page
Tag: Blanking
 
(6 intermediate revisions by 2 users not shown)
Line 1: Line 1:
; Question 1
: I remember you said that you don't like Al as masking material because it will get sputtered off (am I
right?) - but what about ALD deposited aluminium oxide - it is, as far as I know, much harder and resistant
than Al..?


;Answer 1
: We don't have experience with ALD deposited aluminium oxide as a mask, however for some ESC
configurations we have seen evidence of sputtering of the alumina uniformity shield surrounding the wafer;
this would lead me to believe that the ALD aluminium oxide could still sputter and cause contamination
issues.