==Deposition of ITO==
ITO (indium tin oxide) can be deposited by sputtering here at DTU Nanolab. An ITO target is used and it may be sputtered either non-reactively in Ar or reactively in a mixture of Ar and O<sub>2</sub>.

We have acquired a lot of knowledge about ITO deposition in our Cluster Lesker system, and results are summarized on a page here:

*[[Specific_Process_Knowledge/Thin_film_deposition/Sputtering of ITO in Sputter-System Metal-Oxide (PC1)|Sputtering of ITO in Sputter-System Metal-Oxide (PC1)]].

==Comparison of the methods for deposition of ITO==
{|border="1" cellspacing="1" cellpadding="3" style="text-align:left;" 
|-

|-
|-style="background:silver; color:black"
!
![[Specific Process Knowledge/Thin film deposition/Lesker|Sputter-System(Lesker)]]
![[Specific_Process_Knowledge/Thin_film_deposition/Cluster-based_multi-chamber_high_vacuum_sputtering_deposition_system|Sputter-System Metal-Oxide(PC1)]]
|-

|-
|-style="background:WhiteSmoke; color:black"
!Generel description
|
*RF sputtering of an ITO target - reactive sputtering possible
|
*RF sputtering of an ITO target - reactive sputtering possible (not recommended due to arching)
*Pulsed DC sputtering of an ITO target - reactive sputtering possible
|-

|-
|-style="background:LightGrey; color:black"
!Stoichiometry
|
*Not known
|
*In:Sn:O ~ 39:3:58 in the [[Specific_Process_Knowledge/Thin_film_deposition/Cluster-based_multi-chamber_high_vacuum_sputtering_deposition_system#Process information|acceptance test]]. Can be tuned by altering deposition conditions.
|-

|-
|-style="background:WhiteSmoke; color:black"
!Film Thickness
|
*few nm - ~ 200 nm
|
*few nm - ~ 1 μm

|-

|-style="background:LightGrey; color:black"
!Deposition rate
|
* 0.5-2 nm/min
|
* at least up to ~ 10 nm/min ([[Specific_Process_Knowledge/Thin_film_deposition/Cluster-based_multi-chamber_high_vacuum_sputtering_deposition_system#Standard_recipe_performance|see conditions]])
|-

|-
|-style="background:WhiteSmoke; color:black"
!Step coverage
|
*unknown
|
*unknown
|-

|-style="background:LightGrey; color:black"
!Process Temperature
|
* Up to 400 °C
|
* Up to 600 °C
|-

|-
|-style="background:LightGrey; color:black"
!Substrate size
|
* chips
* 1x 100 mm wafer
* 1x 150 mm wafer
|
* chips
* 10x 100 mm wafer
* 10x 150 mm wafer
|-

|-
|-style="background:WhiteSmoke; color:black"
!'''Allowed materials'''
|
*almost any
|
*almost any that does not degas. Note special carrier for III-V materials. See [http://labmanager.dtu.dk/function.php?module=XcMachineaction&view=edit&MachID=441 cross-contamination sheet].
|-
|}