Specific Process Knowledge/Thin film deposition/Furnace LPCVD PolySilicon/Boron doped poly-Si and a-Si: Difference between revisions
| Line 52: | Line 52: | ||
'''Test wafer position:''' Center of the boat | '''Test wafer position:''' Center of the boat | ||
A better uniformity was achieved by annealing in N<sub>2</sub>. Measured film thickness was 370 nm and the sheet resistance was measured to 200 Ω/sq +/- 15 Ω/sq. | A better uniformity was achieved by annealing subsequently in N<sub>2</sub>, the annealing was done in Anneal Oxide Furnace (C1). Measured film thickness was 370 nm and the sheet resistance was measured to 200 Ω/sq +/- 15 Ω/sq. | ||