Specific Process Knowledge/Thermal Process/A3 Phosphor Drive-in furnace: Difference between revisions
| Line 99: | Line 99: | ||
|- | |- | ||
!style="background:silver; color:black" align="center"|Performance | !style="background:silver; color:black" align="center"|Performance | ||
|style="background:LightGrey; color:black"|Film thickness | |style="background:LightGrey; color:black"|Film thickness and quality | ||
|style="background:WhiteSmoke; color:black"| | |style="background:WhiteSmoke; color:black"| | ||
*Dry oxide: ~ 0 nm - 300 nm (it takes too long to grow a thicker oxide) | *Dry oxide: ~ 0 nm - 300 nm (it takes too long to grow a thicker oxide) | ||
*Wet oxide: ~ 0 nm - 3 µm (23 hours wet oxidation at 1100 <sup>o</sup>C for Si[100] wafers) | *Wet oxide: ~ 0 nm - 3 µm (23 hours wet oxidation at 1100 <sup>o</sup>C for Si[100] wafers) | ||
* [[Specific Process Knowledge/Thermal Process/Oxidation/Breakdown voltage measurements/A3 furnace break-down voltage measurement results|Break-down voltage measurement results]] | |||
|- | |- | ||
!style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range | !style="background:silver; color:black" align="center" valign="center" rowspan="3"|Process parameter range | ||