Doping your wafer

This page is about doping your wafer or making a thin film layer doped with boron, phosphorous or Germanium.

Dope with Phosphorous - Doping Silicon wafers with phosphorous by thermal predeposition and drive-in
Dope with Boron - Doping Silicon wafers with boron by thermal predeposition and drive-in
Furnace LPCVD PolySilicon - Deposition of PolySi doped with B or P
PECVD - Making boron glass (BSG), phosphorus glass (PSG), boron-phosphorous glass PBSG or germanium doped glass
Ion implantation

Comparison of different doping processes

	Phosphorous predep	Boron predep	PECVD doped thin film	Doped Poly Si
Generel description	Dopants introduced by diffusion from gas-phase (POCl₃). A thin phosphorous glass is formed on the substrate and phosphorous atoms are driven in. The phosphorous glass is afterward removed by a short BHF etch. Often further annealing is desired in order to redistribute the dopants in the material. This is done in either high temperature annealing furnaces or by rapid thermal annealing.	Dopants introduced by diffusion from solid source wafers. A boron glass is formed on the substrate and boron atoms are driven in. The boron glass is afterward removed by a dry oxidation process in the boron drive in furnace (A1) followed by a BHF etch. Often further annealing is desired in order to redistribute the dopants in the material. This is done in either high temperature annealing furnaces or by rapid thermal annealing.	Deposition of doped thin film (oxides or nitrides). A high temperature step to drive in and redistribute the dopants in the material is required. This is typically done at 800°C - 1100°C in either high temperature annealing furnaces (C1 or C3) or by rapid thermal annealing. The doped glass can afterwards be removed in a BHF etch.	Dopants introduced by in-situ doping of poly/amorphous Si. In some cases you need a high temperature step to redistribute the dopants in the material and alter the crystallinity. This is typically done at 800°C - 1150°C in either high temperature annealing furnaces (C1 or C3) or by rapid thermal annealing.
Process Temperature	900°C - 1150°C	1050°C - 1125°C	300°C	560°C - 620°C
Dopant	Phosporous (POCl₃)	Boron (solid source wafers containing B₂O₃)	Phosphorous (PH₃) Boron (B₂H₆) Germanium (GeH₄)	Phosphorous (PH₃) Boron (B₂H₆ or BCl₃)
Substrate size	100 mm wafers 50 mm wafers	100 mm wafers 50 mm wafers	small samples 50 mm wafers 100 mm wafers 150 mm wafers	100 mm wafers (Boron and Phosphorous) 150 mm wafers (only Boron)
Allowed materials	Silicon Poly/amorphous silicon Oxide Nitride	Silicon Poly/amorphous silicon Oxide Nitride	Silicon Poly/amorphous silicon Oxide Nitride	Silicon Poly/amorphous silicon Oxide Nitride

Ion implantation

Ion implantation cannot be done at Danchip. IBS offers ion-beam implantation as a service. See more at the homepage of IBS: http://www.ion-beam-services.com/about_us.htm