Specific Process Knowledge/Etch/Wet III-V Etches

Unless anything else is stated, everything on this page, text and pictures are made by DTU Nanolab.

All links to Kemibrug (SDS) and Labmanager Including APV and QC requires login.

Feedback to this page: click here

This is a collection of III-V wet-etches; the rates should be tested before use. Make sure you have the proper education in mixing of chemicals before use. Wet etching of III-V materials is primarily to be done in 'Fume hood 07: III-V acids/bases'. Contact information, risk assessment and manual regarding this fume hood can be found in LabManager:

Fume hood 07 Info page in LabManager
It is very important that you dispose off chemicals and process waste according to DTU Nanolab regulations and risk assessments for your work.

'Fume hood 07' in cleanroom D3

For dry etching III-V materials see

• III-V ICP
• III-V RIE - Plassys

InP or GaAs substrate etching

When etching InP or GaAs substrates, both 2” wafers and small pieces, you should collect the used chemicals in a waste bottle. This does not apply for etching epilayers.

There should be two bottles in the fumehood one for HCl used to etch InP substrates and one for citric acid: H2O2 or H2SO4 (10%):H2O2 used to etch GaAs substrates. Once the bottles are full, you should bring them in the basement of building 346 and have a new one in CR. For the GaAs waste you should use empty H2O2 bottles (since they should have a special lid that avoid overpressure), while for InP waste we can use an empty and clean developer bottle.

HCl:H3PO4 etch

HCl(37%):H₃PO₄(85%) is a selective, anisotropic and slow etching of InP. Very slow rate in InGaAsP. The etch rates depend on the orientation of the features and have not yet been calibrated at DTU Nanolab.

See rates below for InP, PQ(1.n) and InGaAs lattice-matched to InP. The acronym PQ(1.n) denotes a lattice-matched InGaAsP on InP with a band gap corresponding to a wavelength of 1.n um.

The temperature is 22 degC +/- 1 degC.

H2SO4:H2O2:H2O etch

H₂SO₄(10%):H₂O₂(30%):H₂O is a selective etch of InGaAsP with very low etch rate in InP. The acronym PQ(1.n) denotes a lattice-matched InGaAsP on InP with a band gap corresponding to a wavelength of 1.n um.

The etch rates have not yet been calibrated at DTU Nanolab. The temperature is 22 degC +/- 1 degC.

Concentrated H2SO4

Concentrated H₂SO₄(98%) is used for deoxidation of InP with a very low etch rate in InGaAsP.

H2SO4(98%) etch rates, nm/min
Etchant	InP	PQ(1.1)	PQ(1.3)	PQ(1.5)	InGaAs
H2SO4(98%)	13	?	<1

H3PO4:H2O2:H2O etch

H₃PO₄(85%):H₂O₂(30%):H₂O is a GaAs/AlGaAs-etch which gives a better surface quality than H₂SO₄-based etches.

BHF, HF etch

BHF etches SiO₂ and partially removes native oxide on InGaAs and InP. Do not use BHF unless you know the dangers involved with this chemical and always use 4H gloves!.

Citric Acid etch

C₆H₈O₇:H₂O₂ is a selective etch of GaAs; does not etch Al_xGa_{1-x}As if x > 0.45.

Solid C₆H₈O₇ is mixed 1:1 by weight with H₂O (30%) using magnetic stirring. The solution C₆H₈O₇:H₂O is thereafter mixed 4:1 volume ratio with H₂O₂.

The above C₆H₈O₇:H₂O₂ solution has an etch-rate of ~360 nm/min in GaAs and < 0.5 nm/min in AlAs @ 25 degC.