Measurement for film thickness

Thickness measurement of thin films can be done by optical measurement methods. At DANCHIP we have three techniques for this: Ellipsometry (ellipsometer), Reflectivity measurement (FilmTek+Optical Profiler) and prism coupling (Prism Coupler). If the thin film is not transparent for light then you must find another way to measure the thickness. You can ex. etch a pattern down to the next layer or substrate and then measure the etch step by profilometry. See description further down.

Measurement of optical constants

Measurement if the optical constants of a thin film is measured together with the thickness of the film either by ellipsometry (using the ellipsometer), by refraction (using the FilmTek) or by prism coupling (using the prism coupler).

Comparing equipment for measuring: thickness and optical constants of optical transparent films

	FilmTek 4000	Ellipsometer	Prism couple	Optical Profiler
Method	Reflection	Ellipsometry	Prism Coupling	Reflection
General description	Thin films up to 250 µm, Especially good for thick thin films and for wafer mapping	Good for very thin films down to a few Å	Best for thin films with refractive index <2.02 and not too thin	Thin films up to 20µm, especially good for measuring in a small point (down to 4µm)
Film thickness range	<250 µm (for silicon oxides > ~75nm)	20 Å to ~2µm (for silicon oxide)	~1-15 µm (silicon oxide@633nm)	~30nm-20µm (down to 10nm when using the base without the microscope)
Film thickness accuracy	Very dependent of how good the model fits (if the fit is good it could be within 1% for a single layer)	Very dependent of how good the model fits.	±(0.5%+50Å)	Very dependent of how good the model fits.(Not so good fitting posibility)
Index range	not any limits	not any limits	<2.02	not any limit
Index accuracy	not known	not known	±0.001	not know
Wavelength range	400-1000 nm	300-950 nm	633nm or 1550 nm	350-950 nm
What kind of thin films can be measured	Any film that is transparent to the light in the given wavelength range ex: Silicon Oxide Silicon nitride PolySilicon Photoresists SU8 Other polymers Very thin layers of metals (<20 nm) and many more	Any film that is transparent to the light in the given wavelength range ex: Silicon Oxide Silicon nitride Very thin layers of PolySilicon Photoresists SU8 Other polymers Very thin layers of metals (<20 nm) and many more	Thin films with refractive index below 2.02	In principle any film that is transparent to the light in the given wavelength range. It is limited by the refractive index files in the software and only one model (Cauchy) ex: Silicon Oxide Silicon nitride PolySilicon Photoresists Other polymers Very thin layers of metals (<20 nm) and many more

Film thickness measurement of Polysilicon film (non-transparent >~4µm): Etch + profilometry method

Can be used to find the thickness for a polysilicon layer on top of a silicon oxide layer. This will however etch away part of the polysilicon layer so you need to use a test wafer.

Procedure:

Etch the polySi away on ½ the wafer in one of the RIE's:
- Place the wafer on a 4" Al-carrier.
- Place ½ a silicon wafer on top.
- Put on the Al-carrier ring to make sure the ½ silicon wafer does not fall off.
- Transfer it to the RIE chamber.
- Select the a Si etch recipe (ex. OH_PolyA, make sure the etch time is long enough).
- Start the etch.
- Watch the end point.
- When the end point occures about the recipe.
- Take out the wafer.
Measure the etch step in one of the profilers.

Feedback to this page: click here

This section is under construction

Name of process

Write a short description of the process and how to perform the process.

Process description using methode 1

Process description using methode 2

Comparison methode 1 and methode 2 for the process

	FilmTek 4000	Ellipsometer	Prism couple	Optical Profiler
Generel description	Thin films up to 250 µm, Especially good for thick thin films and for wafer mapping	Good for very thin films down to a few Å	Best for thin films with refractive index <2.02 and not too thin	Thin films up to 20µm, especially good for measuring in a small point (down to 4µm)
Method	Reflection	Ellipsometry	Prism Coupling	Reflection
Film thickness range	<250 µm (for silicon oxides > ~75nm)	20 Å to ~2µm (for silicon oxide)	~1-15 µm (silicon oxide@633nm)	~30nm-20µm (down to 10nm when using the base without the microscope)
Film thickness accuracy	Very dependent of how good the model fits (if the fit is good it could be within 1% for a single layer)	Very dependent of how good the model fits.	±(0.5%+50Å)	Very dependent of how good the model fits.(Not so good fitting posibility)
Substrate size	# small samples # 50 mm wafers # 100 mm wafers # 150 mm wafers	# small samples # 50 mm wafers # 100 mm wafers # 150 mm wafers
Allowed materials	Allowed material 1 Allowed material 2	Allowed material 1 Allowed material 2 Allowed material 3