Specific Process Knowledge/Thin film deposition/Deposition of Niobium Titanium Nitride

From LabAdviser


Feedback to this page: click here

Unless otherwise stated, this page is written by DTU Nanolab internal

Deposition of Niobium Titanium Nitride

Deposition of NbTiN can be done by reactive sputtering.

The preferred tool for this application is the Cluster-based multi-chamber high vacuum sputtering deposition system, commonly referred to as the 'Cluster Lesker.' The operating process is thoroughly documented and described in detail.:

Comparison of LPCVD, PECVD, and sputter systems for silicon nitride deposition

Sputter-System Metal-Nitride(PC3) Lesker sputter system
Generel description
  • Pulsed DC reactive sputtering
  • Reactive HIPIMS (high-power impulse magnetron sputtering) (require a different target)
  • Reactive DC sputtering (not tested)
Stoichiometry
  • NbxTyN (Sputter-System Metal-Nitride(PC3))

Tunable composition

  • Unknown
Film thickness
  • Limited by process time.
  • Deposition rate (0.18 nm/s) likely faster than Sputter-System (Lesker)
  • Limited by process time.
  • Deposition rate unknown
Process temperature
  • Up to 600 °C
  • Up to 400 °C
Step coverage
  • Some step coverage possible
  • Some step coverage possible but amount unknown
Film quality
  • Deposition on one side of the substrate
  • Properties including tunable stoichiometry (requires process development)
  • Deposition on one side of the substrate
  • Unknown quality
  • Likely O-contamination
Batch size
  • Many smaller samples
  • Up to 10*100 mm or 150 mm wafers
  • Several smaller samples
  • 1-several 50 mm wafers
  • 1*100 mm wafers
  • 1*150 mm wafer
Allowed materials
  • Almost any as long as they do not outgas and are not very toxic, see cross-contamination sheets
  • Almost any as long as they do not outgas and are not very toxic, see cross-contamination sheets