Specific Process Knowledge/Etch/KOH Etch

KOH etch - Anisotropic silicon etch

KOH belongs to the family of anisotropic Si-etchants based on aqueous alkaline solutions. The anisotropy stems from the different etch rates in different crystal directions. The {111}-planes are almost inert whereas the etch rates of e.g. {100}- and {110}-planes are several orders of magnitude faster.

KOH-etching is a highly versatile and cheap way to realize micromechanical structures if you can live with the necessary Si $_{3}$ N $_{4}$ - or SiO $_{2}$ masking materials and the K contamination of the surface. The latter necessitates in most cases a wet post-clean ('7-up' or RCA-clean) if the wafer is to be processed further.

At Danchip we use as a standard a 28 wt% KOH. The etch rate - and the selectivity towards a SiO $_{2}$ -mask - is depending on the temperature. We normally use T=80 ^oC but may choose to reduce this to e.g. 60 ^oC or 70 ^oC in case of a high-precission timed etch (e.g. defining a thin membrane). In some cases we recommend to saturate the standard 28 wt% KOH with IPA with an etch temperature at T=70 ^oC (reduce evaporation of IPA). One example is for boron etch-stop, where the selectivity towards the boron-doped silicon is improved compared to the standard etch. Key facts for the two solutions are resumed in the table:

KOH solutions

	28 wt% KOH	28 wt% KOH sat. with IPA
General description	Etch of Si(100)	Etch of Si(100) with boron etch-stop
Chemical solution	KOH:H $_{2}$ O 500 g : 1000 ml	KOH:H $_{2}$ O:IPA 500 g : 1000 ml : ?? ml
Process temperature	60 ^oC 70 ^oC 80 ^oC (standard - fast etch)	70 ^oC
Possible masking materials:	Stoichiometric Si $_{3}$ N $_{4}$ Si-rich Si $_{3}$ N $_{4}$ PECVD Si $_{3}$ N $_{4}$ Thermal SiO $_{2}$	Stoichiometric Si $_{3}$ N $_{4}$ Si-rich Si $_{3}$ N $_{4}$ PECVD Si $_{3}$ N $_{4}$ Thermal SiO $_{2}$
Etch rate	~0.4 µm/min (60 ^oC) ~0.7 µm/min (70 ^oC) ~1.3 µm/min (80 ^oC)	~0.2 µm/min (70 ^oC) in p⁺⁺ (doping level > 5x10¹⁹ cm^-3)
Roughness	Typical: 100-600 Å	May form hillocks (pyramidal)
Batch size	1-25 wafers at a time	1-25 wafer at a time
Size of substrate	4" wafers	4" wafers
Allowed materials	Silicon Silicon Oxide Silicon Nitride Silicon Oxynitride	Silicon Silicon Oxide Silicon Nitride Silicon Oxynitride

Definition of structures

Due to the almost inert (111)-planes.....

Definition of <110> alignment structures

The etch rate dependence on the crystallographic planes can be used to determine the <110> crystal directions with high precision (better than +/- 0.05 ^o). A fast method for doing this, using the symmetric under-etching behaviour around but not at the <110>-directions, was described by Vangbo and Bäcklund in J. Micromech. Microeng.6 (1996), 279-284. High-precision control of the <110>-direction during alignment can be necessary in order to control the dimensions of KOH-etched structures (e.g. precise control of V-groove dimensions). A dedicated mask (MASK NAME) has been designed for this purpose.

Etch rates: Empirical formula (Seidl et al)

The folowing empirical formula can be used for concentrations in the range of 10-60 wt%:

R = k₀ [H₂O]⁴ [KOH]^0.25 e^-E_a/kT,

where k₀ = 2480 µm/hr (mol/l)^-4.25, E_a = 0.595 eV for Si(100) and k₀ = 4500 µm/hr (mol/l)^-4.25, E_a = 0.60 eV for Si(110)